- Special Metals UDIMET® alloy R41 Ni-Cr Alloy
Special Metals UDIMET® alloy R41 Ni-Cr Alloy
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | UDIMET® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals UDIMET® alloy R41 Ni-Cr Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UDIMET® alloy R41 (UNS N07041) is a precipitation-hardenable nickel-chromium alloy containing significant amounts of cobalt and molybdenum, along with lesser amounts of aluminum and titanium. Alloy R41 exhibits extremely high room and elevated temperature mechanical properties. Excellent corrosion resistance and fabricability have led to wide usage in critical aircraft engine components such as nozzle partitions, turbine blades and wheels, combustion chamber liners and structural hardware.Information Provided by Special Metals Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.25 g/cc | 0.298 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Rupture Strength | 76.0 MPa @Temperature 927 °C, Time 3.60e+6 sec |
11000 psi @Temperature 1700 °F, Time 1000 hour |
|
| 117 MPa @Temperature 871 °C, Time 3.60e+6 sec |
17000 psi @Temperature 1600 °F, Time 1000 hour |
||
| 200 MPa @Temperature 816 °C, Time 3.60e+6 sec |
29000 psi @Temperature 1500 °F, Time 1000 hour |
||
| 345 MPa @Temperature 760 °C, Time 3.60e+6 sec |
50000 psi @Temperature 1400 °F, Time 1000 hour |
||
| 550 MPa @Temperature 704 °C, Time 3.60e+6 sec |
79800 psi @Temperature 1300 °F, Time 1000 hour |
||
| 705 MPa @Temperature 649 °C, Time 3.60e+6 sec |
102000 psi @Temperature 1200 °F, Time 1000 hour |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.9 µm/m-°C @Temperature 93.0 °C |
6.61 µin/in-°F @Temperature 199 °F |
|
| Specific Heat Capacity | 0.435 J/g-°C | 0.104 BTU/lb-°F | |
| Thermal Conductivity | 9.00 W/m-K | 62.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1232 - 1391 °C | 2250 - 2536 °F | |
| Solidus | 1232 °C | 2250 °F | |
| Liquidus | 1391 °C | 2536 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 1.4 - 1.8 % | 1.4 - 1.8 % | |
| Boron, B | 0.0030 - 0.010 % | 0.0030 - 0.010 % | |
| Carbon, C | <= 0.12 % | <= 0.12 % | |
| Chromium, Cr | 18 - 20 % | 18 - 20 % | |
| Cobalt, Co | 10 - 12 % | 10 - 12 % | |
| Iron, Fe | <= 5.0 % | <= 5.0 % | |
| Molybdenum, Mo | 9.0 - 10.5 % | 9.0 - 10.5 % | |
| Nickel, Ni | 47.27 - 58.597 % | 47.27 - 58.597 % | Balance |
| Titanium, Ti | 3.0 - 3.3 % | 3.0 - 3.3 % |
Users viewing this material also viewed the following:
- Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F)
- Solvay Specialty Polymers Radel® R-5000 Polyphenylsulfone (PPSU)
- Techmer ES Luriblend® ABS TL2
- EMS-Grivory Grivory® BG-30 FC PA6-GF30
- DuPont Teijin Films Mylar® EL Polyester Film, 400 Gauge
- Entec Hylex® P1025L1 HB Polycarbonate
- Adell BT-14 Nylon 6, 20% Glass Reinforced; Impact Modified
- SABIC Innovative Plastics LNP LUBRICOMP DFL329 PC
- Ineos J50-1000-181 HDPE
Copyright © lookpolymers.com All Rights Reserved