Plenco 6802 Phenolic, Granular, Transfer Molded (discontinued **)
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Mineral Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plenco 6802 Phenolic, Granular, Transfer Molded
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Two-Stage Phenolic. PLENCO 06802 is a mica and mineral filled novolac phenolic molding compound. Available in Brown.Information supplied by Plenco
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.85 g/cc | 0.0668 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.890 g/cc | 0.0322 lb/in³ | Apparent density per ASTM D1895 |
| Water Absorption | 0.030 % | 0.030 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0039 cm/cm | 0.0039 in/in | per ATM D955. Post shrinkage is 0.07% at 72hr 120ºC per ASTM D1299. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 74 | 74 | ASTM D785 |
| Tensile Strength, Ultimate | 46.0 MPa | 6670 psi | ASTM D638 |
| Elongation at Break | 0.47 % | 0.47 % | ASTM D638 |
| Tensile Modulus | 12.98 GPa | 1883 ksi | ASTM D638 |
| Flexural Yield Strength | 89.8 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 14.36 GPa | 2083 ksi | ASTM D790 |
| Compressive Yield Strength | 174.2 MPa | 25270 psi | ASTM D695 |
| Poissons Ratio | 0.27 | 0.27 | In tension |
| Shear Modulus | 5.12 GPa | 743 ksi | Calculated |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ASTM D256 |
| Impact | 71 | 71 | J/m Plenco drop ball test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 37.0 µm/m-°C @Temperature 20.0 °C |
20.6 µin/in-°F @Temperature 68.0 °F |
|
| Maximum Service Temperature, Air | 202 °C | 396 °F | Heat resistance per ASTM D794 |
| Deflection Temperature at 1.8 MPa (264 psi) | 164 °C | 327 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 3.646e+12 ohm-cm | 3.646e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.9 @Frequency 1e+6 Hz |
4.9 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | Short Time; ASTM D149 |
| Dissipation Factor | 0.041 @Frequency 1e+6 Hz |
0.041 @Frequency 1e+6 Hz |
ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 |
Users viewing this material also viewed the following:
- ICO Polymers ICORENEâ„¢ 195-1325 LMDPE Rotational Molding Resin
- Sumitomo Bakelite North America E 8353-706R-1 Hardware Grade Epoxy
- Schmolz + Bickenbach Thermodur® 2365 EFS Extra Fine Structure - Hot Work Die Steel
- Chase Plastics CP Pryme® PC110GR Polycarbonate, 10% Glass Fiber Reinforced, Mold Release
- CPC - Vycom VINTEC I® PVC Polyvinyl Chloride (PVC)
- Diamond Polymers ABS 3500 Natural 1050
- 3M FM53R2 White Polyester Label Products
- A. Schulman POLYFORT™ FPP 1220 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved