Stellar Canada CERAMITE® BKR-S Wear Resistant Castable

Category Ceramic , Oxide , Aluminum Oxide
Manufacturer Stellar Canada
Trade Name CERAMITE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Stellar Canada CERAMITE® BKR-S Wear Resistant Castable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ceramite is a family of wear resistant castables with a unique combination of high wear resistance, thermal resistance and mechanical strength. Ceramite is produced and supplied to end users world wide, both as mortars and as various precast components. Ceramite can easily be mixed, cast and shaped in any size and is thus comfortably to work with in-situ. Ceramite can be used in within a wide range of temperatures and applications exposed to thermal shock conditions in industries like for example aluminum, cement and ferro.Applications: Floor Tile, Hearth/Furnace Tile, Furnace Sills & Doors, Lintels, Pipe and Duct Linings, Feed Tubes, Troughs/Launders, Ladles, Dampers, Nozzle Blasters, Crucible Linings, Vortex, Burner Tip Cooler Plates, Nose Ring, Electrical Insulation, Cold Wear AreasSpecific Notes on This Grade: The basic all-round castable with good thermal and electrical insulating properties. A castable widely used in aluminum, ferro alloys, mining, cement, and steel industries. Good references as floor times, crucible linings, impact plates, lining of furnace gates etc...Information provided by Stellar Canada.
Physical Properties Metric English Comments
Bulk Density 2.90 g/cc
0.105 lb/in³
Self-flowing
Mechanical Properties Metric English Comments
Modulus of Rupture 0.02600 GPa
3.771 ksi
Hot, prefired at 1832°F/24 hours (1000°C)
Flexural Strength 19.90 MPa

@Temperature 850.0 °C
2886 psi

@Temperature 1562 °F
after Firing; ASTM-349
21.06 MPa

@Temperature 1200 °C
3055 psi

@Temperature 2192 °F
after Firing; ASTM-349
22.2 MPa

@Temperature 1000 °C
3220 psi

@Temperature 1832 °F
after Firing; ASTM-349
23.12 MPa

@Temperature 500 °C
3353 psi

@Temperature 932 °F
after Firing; ASTM-349
Compressive Strength 139.01 MPa

@Temperature 1200 °C
20161 psi

@Temperature 2190 °F
after Firing; ASTM C-349
142.00 MPa

@Temperature 1000 °C
20596 psi

@Temperature 1830 °F
after Firing; ASTM C-349
145.00 MPa

@Temperature 850 °C
21031 psi

@Temperature 1560 °F
after Firing; ASTM C-349
149.00 MPa

@Temperature 20.0 °C
21611 psi

@Temperature 68.0 °F
after 7 days
215.01 MPa

@Temperature 500 °C
31184 psi

@Temperature 932 °F
after Firing; ASTM C-349
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 1200 °C
2192 °F
Component Elements Properties Metric English Comments
Al2O3 79 %
79 %
CaO 4.3 %
4.3 %
Fe2O3 1.0 %
1.0 %
K2O 0.15 %
0.15 %
MgO 0.090 %
0.090 %
Na2O 0.12 %
0.12 %
SiO2 13 %
13 %
TiO2 2.0 %
2.0 %
Descriptive Properties Value Comments
Application Prefired
Precast Shapes