PolyOne Geon™ Vinyl Rigid Extrusion L4857 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L4857 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 42.7 MPa | 6190 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.45 GPa | 355 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 77.9 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 2.00 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
3.75 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A |
| 2.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
4.12 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A | |
| Dart Drop Total Energy | 53.4 J/cm @Temperature 23.0 °C |
0.100 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 187 J/cm @Temperature 23.0 °C |
0.350 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 59.0 µm/m-°C | 32.8 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.8 °C @Thickness 3.18 mm |
163 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Good | |
| Features | Good Weather Resistance | |
| High Impact Resistance | ||
| Low Gloss | ||
| Forms | Cube | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 1-41432-33 | ASTM D4216 |
| 16334 | ASTM D1784 | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Outdoor Applications | |
| Profiles |
Users viewing this material also viewed the following:
- Manifattura Cattaneo PET+PTFE Polyethylene Terephthalate
- Solvay TECHNYL® A 218 V35 PA66, 35% glass fiber, Conditioned
- Samsung Cheil Industries Starex® VS-0826 ABS, Unreinforced FR
- Chengdu Polyster 5500 General Grade TPV
- EMS-Grivory Grivory® LV-5H PA12-GF50
- DuPont™ Tedlar® SP TTRJ10SH9 Clear Polyvinyl Fluoride Film
- Dow Corning 5580 Performance Modifier
- Aclo Accutech Polypropylene Homopolymer HP0336G25M5CL Glass/Mineral Reinforced Coupled
- Ashley Polymers Ashlene® P123 PBT Polyester, 15% Glass Reinforced
- ATI Allegheny Ludlum AL 2205™ Duplex Stainless Steel, Sheet and Strip < 0.1875", UNS S31803
Copyright © lookpolymers.com All Rights Reserved