Special Metals INCOLOY® Alloy 330
| Category | Metal , Superalloy , Iron Base |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCOLOY® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCOLOY® Alloy 330.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A nickel-iron-chromium alloy with an addition of silicon for enhanced oxidation resistance. It has good strength at high temperatures and excellent resistance to carburizing and oxidizing atmospheres. The alloy's austenitic microstructure remains stable during long-time exposure to high temperature. Used in industrial heating for furnace muffles, retorts, and conveyor systems and for heat-treating baskets and fixtures. Standard product forms are round, flats, forging stock, plate, sheet, strip, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.08 g/cc | 0.292 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 600 MPa | 87000 psi | Annealed prior to test |
| 480 MPa @Temperature 550 °C |
69600 psi @Temperature 1020 °F |
Annealed prior to test | |
| Tensile Strength, Yield | 280 MPa @Strain 0.200 % |
40600 psi @Strain 0.200 % |
Annealed prior to test |
| 170 MPa @Strain 0.200 %, Temperature 550 °C |
24700 psi @Strain 0.200 %, Temperature 1020 °F |
Annealed prior to test | |
| Elongation at Break | 45 % | 45 % | Annealed prior to test. |
| 45 % @Temperature 550 °C |
45 % @Temperature 1020 °F |
Annealed prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.9 µm/m-°C @Temperature 20.0 - 100 °C |
8.28 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.460 J/g-°C | 0.110 BTU/lb-°F | |
| Thermal Conductivity | 12.4 W/m-K | 86.1 BTU-in/hr-ft²-°F | |
| Melting Point | 1345 - 1425 °C | 2453 - 2597 °F | |
| Solidus | 1345 °C | 2453 °F | |
| Liquidus | 1425 °C | 2597 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.080 % | <= 0.080 % | |
| Chromium, Cr | 17 - 20 % | 17 - 20 % | |
| Iron, Fe | 43 % | 43 % | As remainder |
| Manganese, Mn | <= 2.0 % | <= 2.0 % | |
| Nickel, Ni | 34 - 37 % | 34 - 37 % | |
| Phosphorous, P | 0.030 % | 0.030 % | |
| Silicon, Si | 0.75 - 1.5 % | 0.75 - 1.5 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0001017 ohm-cm | 0.0001017 ohm-cm | |
| Magnetic Permeability | 1.02 | 1.02 | at 200 oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Polyplastic Armlen® PP-2FR Polypropylene, Flame Retardant
- ND Industries SuperGlue Ethyl 300
- Schott N-KF9 Glass
- SGL Carbon Group SIGRAFIL C® C25 P250 EPY Pelletized Carbon Fiber, Epoxy Sizing
- Silberline EternaBrite® 651-DL
- SABIC Innovative Plastics NORYL GFN3L PPE+HIPS (Asia Pacific)
- Westlake Epolene® C-15P Coating Grade - Branched Medium Molecular Weight Polyethylene Polymer
- CP-Polymer-Technik Wellamid® 6000 GS 30 HWUVCP 30% Glass Sphere Filled Nylon 6, UV Stabilized, Heat Stabilized, Dry
- Crucible Steel AISI 6150 Alloy Steel
- A. Schulman ComAlloy Comtuf® 618 Nylon 6, Mineral Reinforced, Impact Modified
Copyright © lookpolymers.com All Rights Reserved