Solvay TECHNYL® eXten D238 V30 Nylon 6,10, 30% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® eXten D238 V30 Nylon 6,10, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL® eXten D 238 V30 is a PA6,10 30% glass fiber reinforced and impact modified suitable for injection molding. TECHNYL® eXten D 238 V30 is based on a partially bio-sourced polyamide 6,10. This material is available in black.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: TECHNYL® eXten D 238 V30 is suitable to the manufacturing of injection molded parts in all sectors of applications. It offers excellent chemical resistance, low water absorption, very good mechanical properties and moldability.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527 Type 1A |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 Type 1A |
| Tensile Modulus | 7.40 GPa | 1070 ksi | ISO 527 Type 1A |
| Flexural Strength | 199 MPa | 28900 psi | ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ISO 178 |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 2.70 J/cm² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
ISO 1210 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210 | |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
ISO 1210 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C | |
| Mixing Zone | 240-250°C |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B GF 30 FRK 3 Polybutylene Terephthalate, 30% Chemically Coupled Glass Fiber, Red Phosphorus Flame Retardant
- SABIC Innovative Plastics ULTEM DH1004 PEI (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP MX92284 PP (Asia Pacific)
- Silberline Sparkle Silvex® 730-15-C
- Excalibar ExCal® CW 325 Calcium Carbonate CaCO3 Powder
- Aclo Accutech Polypropylene HP0335G30CHIV Homopolymer Glass Reinforced High Impact Coupled
- 3M Scotch-Weld™ DP608 Structural Adhesive
- Ashley Polymers Ashlene® PPO Resin P259
- LyondellBasell Hifax™ CA186 Thermoplastic Olefin Resin
Copyright © lookpolymers.com All Rights Reserved