Solvay TECHNYL® C 52G3 MZ25 PA6, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 52G3 MZ25 PA6, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Flame retardant polyamide PA6 reinforced with mineral filler, for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Applications: This phosphorus and halogen free flame retardant grade is particularly suitable for equipment with robust glow wire resistance such as MCB housings. This grade is available in grey color.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183/A |
| Water Absorption | 1.0 % @Temperature 23.0 °C, Time 86400 sec |
1.0 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 Type 1A |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 Type 1A |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527 Type 1A |
| Flexural Strength | 136 MPa | 19700 psi | ISO 178 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ISO 75/Af |
| Flammability, UL94 | V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
1210 |
| V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
1210 | |
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
1210 | |
| Oxygen Index | 31 % | 31 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
ISO 60695-2-12 |
| 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 220 - 230 °C | 428 - 446 °F | |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® BFL2015 PC
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 285ºF Cure Temperature
- Momentive Performance Materials Siloprenâ„¢ LSR 2345/07 Liquid Silicone Rubber - Specialty Coating
- Haveg 41NA Phenolic; Silicate Filled
- Sumitomo Bakelite North America E 8398 Hardware Grade Epoxy
- Styrolution Absolac® 120 ABS
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N990 Filler
- Dow Corning SILASTIC® 9412/50E KIT PARTS A&B
- Parker Chomerics CHO-SHIELD® 1091 Adhesion Promoter for Conductive Polyurethane Coatings
Copyright © lookpolymers.com All Rights Reserved