Solvay TECHNYL® C 216 V35 Black Z PA6, 35% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 216 V35 Black Z PA6, 35% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide PA6 , reinforced with 35 % of glass fiber, for injection molding.Available in: North AmericaProduct Applications: It has good mechanical properties, it is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. It is used in the automotive industry and electrical sectors.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183/A |
| Water Absorption | 0.90 % @Temperature 23.0 °C, Time 86400 sec |
0.90 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 195 MPa | 28300 psi | ISO 527 Type 1A |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527 Type 1A |
| Tensile Modulus | 10.6 GPa | 1540 ksi | ISO 527 Type 1A |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 10.2 J/cm² | 48.5 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 11.65 J/cm² | 55.44 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
15.6 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.8 | 3.8 | IEC 60250 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | Solution A; IEC 60112 |
Users viewing this material also viewed the following:
- Osprey Metals 4365 Low Alloy Steel Powder (Grade 80% - 22)
- Indium Corp. Indalloy® 164 Pb-In-Ag Solder Alloy
- Inno-Comp INNOPOL® CS 2-5000 Polypropylene Block-Copolymer
- Latrobe LSSâ„¢ H12 Hot Work Tool Steel (ASTM H12)
- SSAB Tunnplat Aluzink F40A Metal-coated Mild Steel
- Sumitomo Bakelite North America E 8940SG Electrical Encapsulation Grade Epoxy
- ExxonMobil LLDPE LL 1002.80 Linear Low Density Polyethylene Resin
- BorsodChem ONGROSTYR F-I Expandable Polystyrene (EPS)
- 3M Scotchkote™ MC 145 Epoxy Primer
- PolyOne Edgetek® AT-25GF-10MN/000 NATURAL Acetal-Copolymer, Glass/Mineral Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved