Solvay Specialty Polymers Udel® GF-110 Polysulfone (PSU), Glass Fiber

Category Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, 10% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Udel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Udel® GF-110 Polysulfone (PSU), Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Udel® GF-110, resin is a 10% glass fiber reinforced polysulfone (PSU). Glass fiber substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the polysulfone resin. The high performance properties and attractive price make these resins particularly effective alternatives to metals in many engineering applications.Features: Acid Resistant; Alcohol Resistant; Alkali Resistant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Strength; High Heat Resistance; High Rigidity; Hydrocarbon Resistant; Hydrolytically StableUses: Appliance Components; Appliances; Connectors; Fittings; Food Service Applications; Industrial Parts; Microwave Cookware; Plumbing Parts; Valves/Valve PartsInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
Melt Flow 6.5 g/10 min

@Load 2.16 kg,
Temperature 343 °C
6.5 g/10 min

@Load 4.76 lb,
Temperature 649 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength 77.9 MPa
11300 psi
ASTM D638
Elongation at Break 4.0 %
4.0 %
ASTM D638
Tensile Modulus 3.72 GPa
540 ksi
ASTM D638
Flexural Strength 128 MPa
18600 psi
ASTM D790
Flexural Modulus 3.79 GPa
550 ksi
ASTM D790
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
ASTM D256
Tensile Impact Strength 101 kJ/m²
48.1 ft-lb/in²
ASTM D1822
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 179 °C
354 °F
Unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 3.18 mm
HB

@Thickness 0.125 in
Electrical Properties Metric English Comments
Volume Resistivity 3.00e+16 ohm-cm
3.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.15

@Frequency 1.00e+6 Hz
3.15

@Frequency 1.00e+6 Hz
ASTM D150
3.18

@Frequency 60.0 Hz
3.18

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 19.0 kV/mm
483 kV/in
ASTM D149
Dissipation Factor 0.00070

@Frequency 60.0 Hz
0.00070

@Frequency 60.0 Hz
ASTM D150
0.0060

@Frequency 1.00e+6 Hz
0.0060

@Frequency 1.00e+6 Hz
ASTM D150
Compliance Properties Metric English Comments
NSF Yes
Yes
NSF 61
Processing Properties Metric English Comments
Melt Temperature 343 - 399 °C
649 - 750 °F
Mold Temperature 121 - 163 °C
250 - 325 °F
Drying Temperature 149 - 163 °C

@Time 10800 - 14400 sec
300 - 325 °F

@Time 3.00 - 4.00 hour
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi
Descriptive Properties Value Comments
Agency Ratings ISO 10993; ISO 10993-Part 1
Availability Asia Pacific
Europe
Latin America
North America
Color Black; Grey; Natural; Opaque
Form Pellets
Injection Rate Fast
Processing Technique Extrusion; Injection Molding
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.0:1.0