Solvay Specialty Polymers AvaSpire® AV-722 SL30 Polyaryletherketone (PAEK)
| Category | Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers AvaSpire® AV-722 SL30 Polyaryletherketone (PAEK).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AV-722 SL30 is a wear resistant grade of AvaSpire® polyaryletherketone (PAEK) designed to provide low wear rates in both non-lubricated and lubricated environments. In addition to the outstanding wear resistance, the resin also offers the outstanding combination of ultra performance attributes commonly known for PEEK. These include: chemical resistance, mechanical strength and stiffness, even at elevated temperatures, as well as long-term and high-temperature thermal-oxidative stability. AV-722 SL30 is formulated with the ternary anti-friction/anti-wear additive system comprised of carbon fiber, graphite, and polytetrafluoroethylene (PTFE.) It offers wear resistance performance comparable to PEEK grades with this modifier system while being more cost-effective.Features: Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Wear Resistance; High Heat ResistanceUses: Automotive Applications; Bearings; Bushings; Oil/Gas Applications; Wear StripInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % @Time 86400 sec |
0.030 % @Time 24.0 hour |
ISO 62 |
| Viscosity | 240000 cP @Shear Rate 1000 1/s, Temperature 400 °C |
240000 cP @Shear Rate 1000 1/s, Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.18 mm |
0.0010 - 0.0030 in/in @Thickness 0.125 in |
|
| Linear Mold Shrinkage, Transverse | 0.017 - 0.019 cm/cm @Thickness 3.18 mm |
0.017 - 0.019 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 1.9 g/10 min | 1.9 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 82 | 82 | ASTM D785 |
| Tensile Strength | 136 MPa | 19700 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 151 MPa | 21900 psi | 5 mm/min, Type 1A; ISO 527-2 |
| Elongation at Break | 2.1 % | 2.1 % | Type 1A, 5 mm/min; ISO 527-2 |
| 2.1 % | 2.1 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 12.4 GPa | 1800 ksi | 5 mm/min; ASTM D638 |
| 15.7 GPa | 2280 ksi | 1 mm/min, Type 1A; ISO 527-2 | |
| Flexural Strength | 209 MPa | 30300 psi | ISO 178 |
| 213 MPa | 30900 psi | ASTM D790 | |
| Flexural Modulus | 10.2 GPa | 1480 ksi | ASTM D790 |
| 13.9 GPa | 2020 ksi | ISO 178 | |
| Compressive Strength | 107 MPa | 15500 psi | ASTM D695 |
| Shear Strength | 71.0 MPa | 10300 psi | ASTM D732 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.50 J/cm | 8.43 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.40 kJ/m² | 3.52 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.34 J/g-°C @Temperature 50.0 °C |
0.320 BTU/lb-°F @Temperature 122 °F |
ASTM C351 |
| 1.81 J/g-°C @Temperature 200 °C |
0.433 BTU/lb-°F @Temperature 392 °F |
ASTM C351 | |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 340 °C | 644 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 267 °C @Thickness 3.20 mm |
513 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 152 °C | 306 °F | DSC |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 354 °C | 669 °F | |
| Middle Barrel Temperature | 366 °C | 691 °F | |
| Front Barrel Temperature | 371 °C | 700 °F | |
| Nozzle Temperature | 374 °C | 705 °F | |
| Melt Temperature | 366 - 388 °C | 691 - 730 °F | |
| Mold Temperature | 149 - 177 °C | 300 - 351 °F | |
| Drying Temperature | 149 °C @Time 14400 sec |
300 °F @Time 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Carbon Fiber + Graphite + PTFE Lubricant | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |
Users viewing this material also viewed the following:
- Advanced Elastomer Systems Trefsin® 3201-65 W305 Thermoplastic Rubber (discontinued **)
- Solvay Specialty Polymers Veradel® AG-230 Polyethersulfone (discontinued **)
- Lehmann & Voss LUVOCOM® 20-7868 Polyphthalamide, with carbon fiber and glass fiber
- Mearthane Durethaneâ„¢ M DM-650A Foam Polyurethane
- SABIC Innovative Plastics LNP Lubricomp ICP36 PA6.12
- Taiwan Sheen Soon Sheenthane® A9030 Thermoplastic Polyurethane Elastomer
- Shakespeare FN-29 Freshwater Nylon Copolymer Fishing Line, 4 lb
- Techmer ES Plastiblend® PBT/ABS GF/M40 FR 40/40% Glass/Mineral Filled
- Zeon Chemicals Nipol® DN4265 Nitrile Elastomer
- Asahi Kasei Delpet® 80N Acrylic Molding Compound, High Heat Grade
Copyright © lookpolymers.com All Rights Reserved