Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK)
| Category | Polymer , Thermoplastic , Polyketone |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AvaSpire® AV-651 is an unreinforced polyaryletherketone (PAEK) that offers more ductility and impact strength than PEEK, with higher chemical and environmental stress cracking resistance than AvaSpire® AV-650. It has been specifically formulated for applications requiring a balance of chemical resistance and mechanical strength along with good part aesthetics, bridging the performance gaps within the ultra polymers space.Features: Autoclave Sterilizable; Biocompatible; Ductile; E-beam Sterilizable; Ethylene Oxide Sterilizable; Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Impact Resistance; Good Sterilizability; Heat Sterilizable; High Heat Resistance; Radiation (Gamma) Resistant; Radiation Sterilizable; Radiotranslucent; Steam Resistant; Steam SterilizableUses: Aerospace Applications; Aircraft Applications; Bearings; Dental Applications; Film; Hospital Goods; Industrial Applications; Medical Devices; Medical/Healthcare Applications; Oil/Gas Applications; Pump Parts; Seals; Surgical InstrumentsInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ISO 62 |
| Viscosity | 240000 cP @Shear Rate 1000 1/s, Temperature 400 °C |
240000 cP @Shear Rate 1000 1/s, Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Thickness 3.18 mm |
0.0070 - 0.0090 in/in @Thickness 0.125 in |
|
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Thickness 3.18 mm |
0.010 - 0.012 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 400 °C |
25 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 94 | 94 | ASTM D785 |
| Tensile Strength | 87.0 MPa | 12600 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 89.0 MPa | 12900 psi | Type 1A, 50 mm/min; ISO 527-2 |
| Elongation at Break | >= 40 % | >= 40 % | Type 1A, 50 mm/min; ISO 527-2 |
| >= 40 % | >= 40 % | 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.7 % | 5.7 % | Type 1A, 50 mm/min; ISO 527-2 |
| 6.2 % | 6.2 % | 50 mm/min; ASTM D638 | |
| Tensile Modulus | 3.00 GPa | 435 ksi | 50 mm/min; ASTM D638 |
| 3.20 GPa | 464 ksi | 1 mm/min, Type 1A; ISO 527-2 | |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| 127 MPa | 18400 psi | ISO 178 | |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| 3.20 GPa | 464 ksi | ISO 178 | |
| Compressive Strength | 112 MPa | 16200 psi | ASTM D695 |
| Shear Strength | 78.0 MPa | 11300 psi | ASTM D732 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Izod Impact, Notched (ISO) | 6.60 kJ/m² | 3.14 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 47.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
26.1 µin/in-°F @Temperature -58.0 - 122 °F |
1 |
| Specific Heat Capacity | 1.31 J/g-°C @Temperature 50.0 °C |
0.313 BTU/lb-°F @Temperature 122 °F |
ASTM C351 |
| 1.82 J/g-°C @Temperature 200 °C |
0.435 BTU/lb-°F @Temperature 392 °F |
ASTM C351 | |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 345 °C | 653 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C @Thickness 3.20 mm |
374 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 158 °C | 316 °F | DSC |
| Flammability, UL94 | V-0 @Thickness 0.800 - 1.60 mm |
V-0 @Thickness 0.0315 - 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+17 ohm-cm | 5.00e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 60.0 Hz |
3.1 @Frequency 60.0 Hz |
ASTM D150 |
| 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| 3.12 @Frequency 1000 Hz |
3.12 @Frequency 1000 Hz |
ASTM D150 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.00 mm |
406 kV/in @Thickness 0.118 in |
ASTM D149 |
| Dissipation Factor | 0.0010 @Frequency 60.0 Hz |
0.0010 @Frequency 60.0 Hz |
ASTM D150 |
| 0.0010 @Frequency 1000 Hz |
0.0010 @Frequency 1000 Hz |
ASTM D150 | |
| 0.0040 @Frequency 1.00e+6 Hz |
0.0040 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 355 °C | 671 °F | |
| Middle Barrel Temperature | 365 °C | 689 °F | |
| Front Barrel Temperature | 370 °C | 698 °F | |
| Nozzle Temperature | 375 °C | 707 °F | |
| Melt Temperature | 365 - 390 °C | 689 - 734 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 150 °C @Time 14400 sec |
302 °F @Time 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | FAA FAR 25.853a; ISO 10993; ISO 10993-Part 1 | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Beige; Natural | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Extrusion Blow Molding | |
| Fiber (Spinning) Extrusion; Film Extrusion | ||
| Injection Blow Molding; Injection Molding | ||
| Machining; Profile Extrusion | ||
| Thermoforming; Wire & Cable Extrusion | ||
| RoHS Compliance | RoHS Compliant | |
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |
Users viewing this material also viewed the following:
- RheTech Products HP525-01 30% Talc Reinforced High Performance Polypropylene, UV Stabilized, Black
- Lucent Polymers PPC-210 Polypropylene, Impact Modified
- Solvay Specialty Polymers Polymist® XPP 515 Polytetrafluoroethylene (PTFE)
- Samsung Cheil Industries Starex® SG-301 Expandable Polystyrene (EPS) High Expansion
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 40 PHR Polyfil HG90 Filler
- Master Bond Supreme 11HT High Temperature Resistant Two Component Epoxy System
- Chevron Phillips Marlex® 9398 HDPE Pipe and Corrugated Extrusion Resin
- Eurotec® Tecodur® PB70 GB20 NL PBT, 20% glass bead reinforced, natural
- Master Bond UV15-7SP4DC One Component, Dual Cured, Flexible UV System
Copyright © lookpolymers.com All Rights Reserved