Silon Taborex TA 1108 HD Chemically-Crosslinkable HDPE Compound
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Crosslinkable |
| Manufacturer | Silon |
| Trade Name | Taborex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Silon Taborex TA 1108 HD Chemically-Crosslinkable HDPE Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TABOREX TA 1108 HD is a crosslinkable compound according to the “SIOPLAS-SYSTEMâ€; made by a Silane grafted ethylene copolymer known as the graft and a Masterbatch containing the crosslinking catalyst. It is used for the production of flexible pipes with an improved surface quality for domestic hot and cold water, under floor heating and central heating application.Information provided by Silon
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.530 g/cc | 0.0191 lb/in³ | DIN 53466 |
| Density | 0.942 g/cc | 0.0340 lb/in³ | DIN 53479/ASTM D1505 |
| Volatiles | <= 0.10 % | <= 0.10 % | ITM-ZP 300CH 3-5-5/d |
| Melt Flow | 2.3 g/10 min @Load 5.00 kg, Temperature 190 °C |
2.3 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133/ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO R 527 |
| Elongation at Break | 250 % | 250 % | ISO R 527 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 160 - 170 °C | 320 - 338 °F | |
| Zone 2 | 170 - 180 °C | 338 - 356 °F | |
| Zone 3 | 170 - 190 °C | 338 - 374 °F | |
| Zone 4 | 170 - 190 °C | 338 - 374 °F | |
| Die Temperature | 190 - 220 °C | 374 - 428 °F | |
| Head Temperature | 200 - 210 °C | 392 - 410 °F | |
| Screw Cooling Temperature | 70.0 - 90.0 °C | 158 - 194 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel content (%) | 75 | EN 579 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SHRINK® Heat Shrink EMI Shielding
- Teknor Apex Sinvicomp SRF 3703 Polyvinyl Chloride, Rigid
- UBE F022NH Polyethylene
- ExxonMobil SAE 40 Mobilgard 1 SHC
- Westlake ELEVATE™ EF529 18.5% Ethylene Vinyl Acetate Copolymer
- Dow UNIVAL™ DMDC-6400 NT 7 High Density Polyethylene Resin (HDPE)
- China-Yixing Longly Refractories Seggar Corundum-Mullite
- Colorite Polymers CS1535UL Wire and Cable Insulation Vinyl Compound
- Abatron AboCast/AboCure 8109-1
- SABIC Innovative Plastics LNP Stat-kon MX01767C PP
Copyright © lookpolymers.com All Rights Reserved