ATI Wah Chang Zircadyne® Alloy Zr 702

Category Metal , Nonferrous Metal , Zirconium Alloy
Manufacturer ATI Wah Chang
Trade Name Zircadyne®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ATI Wah Chang Zircadyne® Alloy Zr 702.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Zircadyne 702 is commercially pure zirconium. Alloy exhibits good ductility even at cryogenic temperatures and good strength comparable with other common engineering alloys.Information provided by ATI Wah Chang
Physical Properties Metric English Comments
Density 6.50 g/cc
0.235 lb/in³
Vapor Pressure 1.20 bar

@Temperature 3600 °C
 900 torr

@Temperature 6510 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 157 MPa

@Temperature 371 °C
 22700 psi

@Temperature 700 °F
198 MPa

@Temperature 316 °C
 28700 psi

@Temperature 601 °F
201 MPa

@Temperature 260 °C
 29100 psi

@Temperature 500 °F
230 MPa

@Temperature 204 °C
 33300 psi

@Temperature 399 °F
305 MPa

@Temperature 149 °C
 44200 psi

@Temperature 300 °F
364 MPa

@Temperature 93.0 °C
 52800 psi

@Temperature 199 °F
468 MPa

@Temperature 23.0 °C
 67900 psi

@Temperature 73.4 °F
Tensile Strength, Yield 82.0 MPa

@Temperature 371 °C
 11900 psi

@Temperature 700 °F
97.2 MPa

@Temperature 316 °C
 14100 psi

@Temperature 601 °F
129 MPa

@Temperature 260 °C
 18700 psi

@Temperature 500 °F
139 MPa

@Temperature 204 °C
 20200 psi

@Temperature 399 °F
196 MPa

@Temperature 149 °C
 28400 psi

@Temperature 300 °F
268 MPa

@Temperature 93.0 °C
 38800 psi

@Temperature 199 °F
321 MPa

@Temperature 23.0 °C
 46600 psi

@Temperature 73.4 °F
Elongation at Break 28.9 %

@Temperature 23.0 °C
 28.9 %

@Temperature 73.4 °F
31.5 %

@Temperature 93.0 °C
 31.5 %

@Temperature 199 °F
40.1 %

@Temperature 316 °C
 40.1 %

@Temperature 601 °F
42.5 %

@Temperature 149 °C
 42.5 %

@Temperature 300 °F
44.1 %

@Temperature 371 °C
 44.1 %

@Temperature 700 °F
49 %

@Temperature 204 °C
 49 %

@Temperature 399 °F
49 %

@Temperature 260 °C
 49 %

@Temperature 500 °F
Modulus of Elasticity 64.1 GPa

@Temperature 371 °C
 9300 ksi

@Temperature 700 °F
69.6 GPa

@Temperature 316 °C
 10100 ksi

@Temperature 601 °F
75.2 GPa

@Temperature 260 °C
 10900 ksi

@Temperature 500 °F
80.7 GPa

@Temperature 204 °C
 11700 ksi

@Temperature 399 °F
86.9 GPa

@Temperature 149 °C
 12600 ksi

@Temperature 300 °F
93.1 GPa

@Temperature 93.0 °C
 13500 ksi

@Temperature 199 °F
98.6 GPa

@Temperature 38.0 °C
 14300 ksi

@Temperature 100 °F
99.2 GPa

@Temperature 23.0 °C
 14400 ksi

@Temperature 73.4 °F
Poissons Ratio 0.35
0.35
Shear Modulus 36.2 GPa

@Temperature 23.0 °C
 5250 ksi

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Heat of Fusion 252.7 J/g
108.7 BTU/lb
Latent
Heat of Vaporization 6490 J/g
2790 BTU/lb
Latent
CTE, linear 6.30 µm/m-°C

@Temperature 149 °C
 3.50 µin/in-°F

@Temperature 300 °F
7.02 µm/m-°C

@Temperature 260 °C
 3.90 µin/in-°F

@Temperature 500 °F
7.38 µm/m-°C

@Temperature 371 °C
 4.10 µin/in-°F

@Temperature 700 °F
Melting Point 1852 °C
3366 °F
Component Elements Properties Metric English Comments
Fe + Cr <= 0.20 %
<= 0.20 %
Hafnium, Hf <= 4.5 %
<= 4.5 %
Zirconium, Zr >= 94.7 %
>= 94.7 %