ExxonMobil Bicor™ 20MB400 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Bicor™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Bicor™ 20MB400 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Bicor 20MB400 is a one side treated, sealable coextruded OPP film. It is designed for use in laminations.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Outstanding optical propertiesGood seal strengthGood dimensional stabilityGood hot slipGood hot tackFeatures:In Lamination Lap SealableApplications:BakeryBiscuits/Cookies/CrackersConfectionery, Chocolate Confectionery, Gum Confectionery, SugarCrisps and SnacksFresh ProduceFrozen FoodHealth and Beauty CareHousehold and DetergentsIce CreamPet Food Uses:HFFS Flexible Packaging Pre-made Bags – Flexible PackagingVFFS Flexible Packaging Processing Method: Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing and Solvent Rotogravure PrintingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 1.40 g/m²/day

@Temperature 23.0 °C
0.0900 g/100 in²/day

@Temperature 73.4 °F
85% RH; ExxonMobil Method
6.98 g/m²/day

@Temperature 38.0 °C
0.450 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Thickness 20.1 microns
0.790 mil
ExxonMobil Method
Coating Weight 17.9 g/m²
11.2 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 205 %
205 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 55 %
55 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 2.00 GPa
290 ksi
MD; ExxonMobil Method
3.50 GPa
508 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.30
0.30
Untreated Surface; ExxonMobil Method
Seal Strength 300 g/25 mm

@Pressure 0.138 MPa,
Temperature 115 °C
300 g/in

@Pressure 20.0 psi,
Temperature 239 °F
EMS, 0.8 sec, Untreated; ExxonMobl Method
Film Tensile Strength at Break, MD 140 MPa
20300 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 290 MPa
42100 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Haze 1.8 %
1.8 %
ExxonMobil Method
Gloss 85 %
85 %
45°; ExxonMobil Method
Descriptive Properties Value Comments
Heat Seal Range 54°F
36.3 psi, 0.2 sec
Yield 38600 in2/lb