Sibur O-40 Compound 239 Polyvinyl Chloride (PVC)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Molded |
| Manufacturer | Sibur |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sibur O-40 Compound 239 Polyvinyl Chloride (PVC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a period of 20 minutes. For insulation of wires and cables operating in intervals of temperatures from -40°C to 70°C.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 - 1.33 g/cc | 0.0441 - 0.0480 lb/in³ | |
| Water Absorption | <= 0.35 % | <= 0.35 % | |
| Collected Volatile Condensable Material | <= 3.0 % | <= 3.0 % | Loss in mass at 160°C during 6 hours |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 14.7 MPa | >= 2130 psi | |
| Elongation at Break | >= 300 % | >= 300 % |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Softening Point | 160 - 180 °C | 320 - 356 °F | |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | |
| Flammability Test | <= 30 | <= 30 | In seconds, method A |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 5.00e+10 ohm-cm @Temperature 20.0 °C |
>= 5.00e+10 ohm-cm @Temperature 68.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Non-colored, black, white | |
| Elongation Retained After Ageing | 80% | Aged for 7 days at 100±2°C |
| Number of Inclusions | <36 psc | With dimensions up to 0.5 mm |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PQ 81 T 30 PP, 30% mineral filling
- Premix Premi-Glas® 3200-22 Fiberglass Reinforced SMC
- Inno-Comp INNOPOL® CS 2-9524 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer
- SABIC Innovative Plastics Valox® 735 PBT
- Schott RG665 Long Pass Filter
- Toho Tenax Besfight® MC Type I (3000 Filament) Nickel Coated Carbon Fiber
- Trelleborg AEM Eccospheres® SI-100 Sodium Borosilicate Glass Microspheres
- American Elements Iron Oxide Nanopowder
- DuPont Bynel® 50E631 Adhesive Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved