DSM Arnitel® EM631 TPC-ET
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Arnitel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Arnitel® EM631 TPC-ET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion Grade
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 0.60 % | 0.60 % | Sim. To ISO 62 |
| Moisture Absorption | 0.200 % | 0.200 % | Sim. To ISO 62 |
| Melt Flow | 6.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
cm<sup>3</sup>/10min Melt Volume-flow Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 @Time 3.00 sec |
61 @Time 0.000833 hour |
ISO 868 |
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ISO 527-1/-2 |
| Tensile Stress | 15.8 MPa @Strain 100 % |
2290 psi @Strain 100 % |
ISO 527-1/-2 |
| 15.9 MPa @Strain 10.0 % |
2310 psi @Strain 10.0 % |
ISO 527-1/-2 | |
| Tensile Modulus | 0.310 GPa | 45.0 ksi | ISO 527-1/-2 |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 185 µm/m-°C | 103 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 185 µm/m-°C | 103 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 212 °C | 414 °F | 10°C/min; ISO 11357-1/-3 |
| Vicat Softening Point | 125 °C | 257 °F | 50 °C/h 10N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz |
3.4 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.8 @Frequency 100 Hz |
3.8 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.011 @Frequency 100 Hz |
0.011 @Frequency 100 Hz |
IEC 60250 |
| 0.034 @Frequency 1.00e+6 Hz |
0.034 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Users viewing this material also viewed the following:
- KB Alloys 10% Zirconium Aluminum Alloy
- Garlock GRAPH-LOCK® 3128 HOCHDRUCK® Graphite Sheet Gasketing, Steel Reinforced
- Global ABS-406 General Purpose ABS
- Polyplastics Freqtis® P0813A (PPS/LCP), Molding Compound
- Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.0015 Phosphoric Acid Anodized Aluminum Honeycomb
- ChevronTexaco Aries® 46
- Aclo Accutech Polypropylene Copolymer CP0437C10L1 Calcium Reinforced
- ArcelorMittal Zagnelis™ ZM90 Double-sided ZnMgAl galvanized steel
Copyright © lookpolymers.com All Rights Reserved