SABIC Innovative Plastics LNP Lubriloy RF206H PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubriloy RF206H PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant, Lubricants. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D 792
1.24 g/cc
0.0448 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.35 %

@Time 86400 sec
 0.35 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0030 - 0.0040 cm/cm

@Time 86400 sec
 0.0030 - 0.0040 in/in

@Time 24.0 hour
 ASTM D 955
0.0032 - 0.0044 cm/cm

@Time 86400 sec
 0.0032 - 0.0044 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.011 - 0.012 cm/cm

@Time 86400 sec
 0.011 - 0.012 in/in

@Time 24.0 hour
 ASTM D 955
0.0109 - 0.0124 cm/cm

@Time 86400 sec
 0.0109 - 0.0124 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 121 MPa
17500 psi
ISO 527
122 MPa
17700 psi
ASTM D 638
Elongation at Break 2.6 %
2.6 %
ASTM D 638
2.7 %
2.7 %
ISO 527
Tensile Modulus 8.20 GPa
1190 ksi
1 mm/min; ISO 527
8.89 GPa
1290 ksi
50 mm/min; ASTM D 638
Flexural Strength 178 MPa
25800 psi
ASTM D 790
192 MPa
27800 psi
ISO 178
Flexural Modulus 6.82 GPa
989 ksi
ASTM D 790
8.50 GPa
1230 ksi
ISO 178
Izod Impact, Notched 1.22 J/cm

@Temperature 23.0 °C
 2.29 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 7.58 J/cm

@Temperature 23.0 °C
 14.2 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature 23.0 °C
 5.71 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 48.0 kJ/m²

@Temperature 23.0 °C
 22.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
12.0 J

@Temperature 23.0 °C
 8.85 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Coefficient of Friction, Dynamic 0.62
0.62
ASTM D 3702 Modified
Coefficient of Friction, Static 0.43
0.43
ASTM D 3702 Modified
K (wear) Factor 58.4 x 10-8 mm³/N-M
29.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 36.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
 20.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
36.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 20.5 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 69.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
69.1 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 258 °C

@Thickness 3.20 mm
 496 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 238 °C
460 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
241 °C

@Thickness 3.20 mm
 466 °F

@Thickness 0.126 in
 unannealed; ASTM D 648