- Sax Polymers SAXAMID 126F6T3 Nylon 6, 30% Glass Fiber and PTFE
Sax Polymers SAXAMID 126F6T3 Nylon 6, 30% Glass Fiber and PTFE
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, PTFE Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 126F6T3 Nylon 6, 30% Glass Fiber and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 126F6T3 is a polyamide 6 injection-molding-grade reinforced with 30% glass fibers and 15% PTFE. Because of its high strength and stiffness this grade is often used for stressed parts requiring low friction - low friction coefficients result in very good wear resistance.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 150 MPa | 21800 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 7.10 GPa | 1030 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 268 MPa | 38900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.10 GPa | 1170 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² @Temperature -30.0 °C |
35.7 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 79.0 kJ/m² @Temperature 23.0 °C |
37.6 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 7.60 J/cm² @Temperature -30.0 °C |
36.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 8.20 J/cm² @Temperature 23.0 °C |
39.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 216 °C | 421 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FC 39 Low Density Polyethylene - Blown Film Extrusion
- Saint-Gobain Vitreosil® Clear Fused Quartz Tubing
- Solvay TECHNYL® B 50 H1 PA66/6, Conditioned
- Shin-Etsu Silicones LIMSâ„¢ KE1950-70A/B Elastomer
- Teknor Apex APEX® 3301-65 Polyvinyl Chloride, Flexible
- Unitika A1030SR PA6, Conditioned
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with TP-95 Plasticizer
Copyright © lookpolymers.com All Rights Reserved