Samyang Triel® 5600 Thermoplastics Polyetherester Elastomer, General Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5600 Thermoplastics Polyetherester Elastomer, General Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5600 is an extrusion grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.017 - 0.020 cm/cm | 0.017 - 0.020 in/in | ASTM D955 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| 12 g/10 min @Load 2.16 kg, Temperature 240 °C |
12 g/10 min @Load 4.76 lb, Temperature 464 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength, Ultimate | 30.9 MPa | 4480 psi | ASTM D638 |
| Tensile Strength, Yield | 14.2 MPa @Strain 5.00 % |
2060 psi @Strain 5.00 % |
ASTM D638 |
| 18.6 MPa @Strain 10.0 % |
2700 psi @Strain 10.0 % |
ASTM D638 | |
| 20.6 MPa @Strain 50.0 % |
2990 psi @Strain 50.0 % |
ASTM D638 | |
| Flexural Yield Strength | 12.3 MPa | 1780 psi | ASTM D790 |
| Flexural Modulus | 0.260 GPa | 37.7 ksi | ASTM D790 |
| Izod Impact, Notched | 1.47 - 1.77 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
2.76 - 3.31 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 3.17 mm, Temperature 23.0 °C |
NB @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 209 °C | 408 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| Vicat Softening Point | 193 °C | 379 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXE171R PC (Europe-Africa-Middle East)
- LG Chemical LUCEL N145-02 General Purpose POM, Unreinforced, Externally Lubricated, Ultra High Flow
- A. Schulman POLYBATCH™ White L8350 HSF Concentrate Based In High-Flow LLDPE
- Denka REOMER G G8070 Thermoplastic Elastomer, For Injection Molding
- Ascend Performance Materials Vydyne® 41 Nylon 66, Conditioned
- BASF Ultramid® SEG7 35% Glass Filled PA6 (Dry)
- 3M Scotch-Weld™ DP5105 Structural Adhesive
- ACC EP MAP-Z 18 EPI Engineered Polymers Aliphatic Polymer
- LATI Latilub 66-15ST G/30 PA66, 30% Glass Fiber Reinforced, Silicone/PTFE Filled
Copyright © lookpolymers.com All Rights Reserved