SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing Carbon Fiber, Silicone, PTFE. Added features of this material include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.930 % | 0.930 % | 50% RH, 24 hrs; ASTM D570 |
| 1.35 % | 1.35 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm @Time 86400 sec |
0.0015 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0043 cm/cm @Time 86400 sec |
0.0043 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 201 MPa | 29200 psi | ASTM D638 |
| 228 MPa | 33100 psi | ISO 527 | |
| Elongation at Break | 1.4 % | 1.4 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 23.1 GPa | 3350 ksi | 1 mm/min; ISO 527 |
| 29.5 GPa | 4280 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 333 MPa | 48300 psi | ASTM D790 |
| 354 MPa | 51300 psi | ISO 178 | |
| Flexural Modulus | 16.4 GPa | 2380 ksi | ASTM D790 |
| 21.3 GPa | 3090 ksi | ISO 178 | |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.45 J/cm | 17.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.25 | 0.25 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.22 | 0.22 | ASTM D3702 Modified |
| K (wear) Factor | 12.1 x 10-8 mm³/N-M | 6.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 231 °C | 448 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 244 °C @Thickness 3.20 mm |
471 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nyco ULTRAFIBRE® M30 Wollastonite
- Kazanorgsintez PC-022 Polycarbonate
- Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes
- Hong Kun Group 4-Cyano-2-Fluorobenzyl bromide Pharmaceutical Intermediate
- Solvay Specialty Polymers Amodel® AT-1116 HS Polyphthalamide (PPA), 16% Glass Fiber (Dry)
- American Elements Tungsten Nanoparticles
- Eagle Brass 735 Nickel Silver 18%, Spring
- Ashley Polymers Ashlene® 745 Nylon 6/69
- Amco PRIMATOP PP HOMO 011 Extrusion Processing Polypropylene
- Polymer Resources PPX-GP6 Modified PPO, General Purpose with HDT of 290 F (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved