- Samyang Triel® 5550 Thermoplastics Polyetherester Elastomer, General Extrusion
Samyang Triel® 5550 Thermoplastics Polyetherester Elastomer, General Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5550 Thermoplastics Polyetherester Elastomer, General Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5550 is an extrusion grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.017 - 0.020 cm/cm | 0.017 - 0.020 in/in | ASTM D955 |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| 11 g/10 min @Load 2.16 kg, Temperature 240 °C |
11 g/10 min @Load 4.76 lb, Temperature 464 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength, Ultimate | 26.5 MPa | 3840 psi | ASTM D638 |
| Tensile Strength, Yield | 10.8 MPa @Strain 5.00 % |
1560 psi @Strain 5.00 % |
ASTM D638 |
| 14.7 MPa @Strain 10.0 % |
2130 psi @Strain 10.0 % |
ASTM D638 | |
| 17.7 MPa @Strain 50.0 % |
2560 psi @Strain 50.0 % |
ASTM D638 | |
| Flexural Yield Strength | 9.32 MPa | 1350 psi | ASTM D790 |
| Flexural Modulus | 0.178 GPa | 25.7 ksi | ASTM D790 |
| Izod Impact, Notched | 2.45 - 2.75 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
4.59 - 5.14 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 3.17 mm, Temperature 23.0 °C |
NB @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 210 °C | 410 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ASTM D648 |
| Vicat Softening Point | 185 °C | 365 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 610 BT N 32 B PA610
- Potters Industries Q-Cel® 300
- SABIC Innovative Plastics EXTEM UH1006 TPI Blend (Europe-Africa-Middle East)
- PolyOne Edgetek® AS-20GF/000 Acrylonitrile Butadiene Styrene (ABS)
- MetalTek MTEK 440A Martensitic Stainless Steel
- A. Schulman POLYBATCH™ Grey 8035 Concentrate Based In Polyethylene
- Zircar Ceramics AL-30AAH Alumina Insulation
- A. Schulman SCHULADUR® A GF50 50% Glass Fiber Reinforced PBT
- China-Yixing Longly Refractories Slab SiC
- BASF Hexamethylenediamine
Copyright © lookpolymers.com All Rights Reserved