- Lehmann & Voss LUVOCOM® 1106-8085/YL Polyether imide, unreinforced, laser markable
Lehmann & Voss LUVOCOM® 1106-8085/YL Polyether imide, unreinforced, laser markable
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1106-8085/YL Polyether imide, unreinforced, laser markable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 115 MPa | 16700 psi | |
| Elongation at Yield | 6.6 % | 6.6 % | |
| 8.2 % | 8.2 % | flexural | |
| Modulus of Elasticity | 3.50 GPa | 508 ksi | |
| Flexural Strength | 165 MPa | 23900 psi | |
| Flexural Modulus | 3.00 GPa | 435 ksi | |
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 380 °C | 716 °F | mass temp |
| Nozzle Temperature | 350 - 400 °C | 662 - 752 °F | |
| Zone 1 | 330 - 350 °C | 626 - 662 °F | |
| Zone 2 | 340 - 390 °C | 644 - 734 °F | |
| Zone 3 | 350 - 400 °C | 662 - 752 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 120 °C @Time >=28800 sec |
248 °F @Time >=8.00 hour |
Dehumidifying dryer |
| 150 °C @Time >=14400 sec |
302 °F @Time >=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | rape yellow |
Users viewing this material also viewed the following:
- Hexion Bakelite™ PF 2400 Phenolic Formaldehyde Resin, High Surface Quality, Dishwasher Proof, UL Listed (disc
- LyondellBasell Alathon® M4661 High Density Polyethylene
- Momentive Performance Materials LVG342 Low Volatile Silicone Adhesive, Mixed, White
- Mueller Alloy 3530 High Leaded Brass 62% (UNS C35300)
- SABIC Innovative Plastics LNP LUBRICOMP LL004E PEEK (Asia Pacific)
- DuPont Keldax® 6868 Filled Thermoplastic Ethylene Polymer
- ATI Allegheny Ludlum 01 Tool Steel, UNS T31501
- Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Dry)
- Asahi Kasei Thermylene® P7-30FG-0874 30% Glass Fiber Reinforced, UV Stabilized
- Beijing Evergrow Resources ER-W-120G Polypropylene Super-Fine Filter Material
Copyright © lookpolymers.com All Rights Reserved