- Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
- Samsung Cheil Industries TRANEX® TX-0520T Transparent Grade ABS
Samsung Cheil Industries TRANEX® TX-0520T Transparent Grade ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | TRANEX® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries TRANEX® TX-0520T Transparent Grade ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 220 °C |
16 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 43.12 MPa @Thickness 3.17 mm |
6254 psi @Thickness 0.125 in |
|
| Elongation at Break | 14 % @Thickness 3.17 mm |
14 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 58.80 MPa @Thickness 3.17 mm |
8528 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 1.93 GPa @Thickness 3.17 mm |
280 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.47 J/cm @Thickness 3.17 mm |
2.75 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.7 % | 2.7 % | ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | Injection Temp |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 75.0 - 80.0 °C | 167 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 68.5 - 107.7 MPa | 9940 - 15620 psi | |
| Back Pressure | 0.979 - 1.96 MPa | 142 - 284 psi | |
| Screw Speed | 60 - 90 rpm | 60 - 90 rpm |
Users viewing this material also viewed the following:
- Karina E CAK 65-48/1 Black PVC Compound
- Teknor Apex APEX® 80873 Polyvinyl Chloride, Semi-Rigid
- Williams Advanced Alloys WS185 Solder
- CoorsTek PlasmaPure-UC™ 99.9% Alumina
- ExxonMobil LDPE LD 104BR Low Density Polyethylene Resin
- EPICHEM Epinyl PA 66 GF 30 Polyamide 66, 30% Glass
- ConocoPhillips Hydroclear® 32 Turbine Oil
- BASF Ultrason® KR 4113 PESU with 10/10% Carbon Fibers/Graphite and 10% PTFE
- Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, Conditioned
Copyright © lookpolymers.com All Rights Reserved