- Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
- Samsung Cheil Industries Starex® WR-9300HF ASA, Unreinforced Heat Resistant
Samsung Cheil Industries Starex® WR-9300HF ASA, Unreinforced Heat Resistant
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® WR-9300HF ASA, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Melt Flow | 15 g/10 min @Load 10.0 kg, Temperature 220 °C |
15 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 107 | 107 | ASTM D785 |
| Tensile Strength, Yield | 45.1 MPa | 6540 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 88 % | 88 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 68.6 MPa | 9950 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.26 GPa | 327 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 3.17 mm |
2.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Yellow Index | 25 % @Thickness 3.20 mm |
25 % @Thickness 0.126 in |
ASTM D1925 |
Users viewing this material also viewed the following:
- MV Labs RU490 [Ru(C10H8N2)3]Cl2·6H2O Tris(2,2'-bipyridyl)dichlororuthenium(II) dichloride hexahydrate
- Reliance Industries Polypropylene Homopolymer
- ExxonMobil Exceed™ 2018CA Blown Film Resin (discontinued **)
- SABIC Innovative Plastics ULTEM 1010TC PEI (Asia Pacific)
- Master Bond EP30-4 Fast Curing Non-Yellowing Two Component Epoxy System
- Hexcel® HexWeb® HDC - 3/16 - 16.0 (R2) Heavy Density Core
- DAK Americas Laser+® HP806 (B93A) PET
- Arlon 55949C028 0.029" (0.737 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved