- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Samsung Cheil Industries Starex® VH-0850 ABS, Unreinforced FR
Samsung Cheil Industries Starex® VH-0850 ABS, Unreinforced FR
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® VH-0850 ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength, Yield | 40.2 MPa | 5830 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 57.9 MPa | 8400 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 2.45 J/cm @Thickness 6.35 mm |
4.59 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C @Thickness 6.40 mm |
167 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 83.0 °C | 181 °F | B/50; ISO R306 |
| Flammability, UL94 | V-0 @Thickness 1.50 - 6.00 mm |
V-0 @Thickness 0.0591 - 0.236 in |
|
| 5VB @Thickness 3.00 mm |
5VB @Thickness 0.118 in |
||
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
Users viewing this material also viewed the following:
- Honeywell ACLAR® 11A (2.00 mil) CTFE Homopolymer, Barrier Film (discontinued **)
- Michelman® Release Coat® P1 Uncatalyzed portion of a two-part silicone release coating
- Borealis Xmod™ GD301FE Polypropylene, Glass Fiber Reinforced
- DuPont Performance Polymers Delrin® 911DP NC010 Acetal (POM) (Unverified Data**)
- Diamond Polymers ABSPC 9802 ABS/PC Molding Grade, High Impact, High Heat
- Dow Corning 409 HS RESIN
- Akzo Nobel Expancel® 091 WE 40 d24 Wet expanded microspheres
- 3M 8992 Polyester Tape
Copyright © lookpolymers.com All Rights Reserved