Samsung Cheil Industries Starex® VE-1805 HIPS, Unreinforced FR

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® VE-1805 HIPS, Unreinforced FR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.145 g/cc
1.145 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0060 in/in

@Thickness 0.126 in
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0060 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 12 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 12 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 22.6 MPa
3270 psi
20 mm/min; ASTM D638
Flexural Strength 29.4 MPa
4260 psi
2.8 mm/min; ASTM D638
Flexural Modulus 1.77 GPa
256 ksi
2.8 mm/min; ASTM D638
Izod Impact, Notched 0.981 J/cm

@Thickness 3.17 mm
 1.84 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 71.0 °C

@Thickness 6.40 mm
 160 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 85.0 °C
185 °F
B/50; ISO R306
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in