Lanxess Durethan® TP 140-009 901510 Nylon 6, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® TP 140-009 901510 Nylon 6, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6 extrusion- and blow molding-grade, 15% glass fibers, elastomer-modified, good heat-ageing resistance, dry-impact modified
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.206 g/cc | 0.04357 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00141 cm/cm | 0.00141 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0066 cm/cm | 0.0066 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Conditioned; ISO 527-1/-2 |
| 104 MPa | 15100 psi | ISO 527-1/-2 | |
| Elongation at Break | 5.3 % | 5.3 % | ISO 527-1/-2 |
| 28 % | 28 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 2.20 GPa | 319 ksi | Conditioned; ISO 527-1/-2 |
| 5.30 GPa | 769 ksi | ISO 527-1/-2 | |
| Impact | 1456 | 1456 | Puncture maximum force (N); ISO 6603-2 |
| 802 @Temperature -30.0 °C |
802 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 | |
| Puncture Energy | 4.20 J | 3.10 ft-lb | ISO 6603-2 |
| 2.30 J @Temperature -30.0 °C |
1.70 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| 2.30 J @Temperature -30.0 °C |
1.70 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 140 µm/m-°C | 77.8 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 219 °C | 426 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C | 399 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 59.0 °C | 138 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| Processing | Blow molding | |
| Sheet extrusion | ||
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Ineos ABS Lustran® QE 1088 FC, Injection Grade (discontinued **)
- Shakespeare WonderThread® M-7 diameter 0.003" Polyester Industrial Sewing Thread
- SABIC Innovative Plastics LNP THERMOCOMP NF004 PC+ABS (Asia Pacific)
- A. Schulman POLYFORT™ FTP 3130H-01/FTP 3130HU-Colors
- ExxonMobil LLDPE LL 1002YB Cast Linear Low Density Polyethylene Resin
- E-Polymers TEKAMID® TB110SG30 30% Glass Fiber Reinforced, High Impact PA6 Resin
- ExxonMobil Escorene™ 768.MJ Blown Ethylene Vinyl Acetate Copolymer
- Asahi Glass Fluon® L170J PTFE Lubricant
- LG Chemical i-BuOH Isobutyl Alcohol
- Plenco 51015 PET, Pellet, Injection Molded, Black (discontinued **)
Copyright © lookpolymers.com All Rights Reserved