Samsung Cheil Industries Starex® NH-0927 ABS, Unreinforced FR
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® NH-0927 ABS, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | 35.3 MPa | 5120 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.9 MPa | 7820 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.26 GPa | 327 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 65.7 MPa | 9530 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.57 J/cm @Thickness 6.35 mm |
2.94 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.77 J/cm @Thickness 3.17 mm |
3.31 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C @Thickness 6.40 mm |
201 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C @Thickness 6.40 mm |
190 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | B/50; ISO R306 |
| 99.0 °C | 210 °F | B/120; ISO R306 | |
| Flammability, UL94 | V-2 @Thickness 1.00 - 3.00 mm |
V-2 @Thickness 0.0394 - 0.118 in |
Users viewing this material also viewed the following:
- MV Labs CS700 CsNO3 Cesium nitrate
- Nanocyl SIZICYL™ XC R2G Liquid Sizing Agent for Carbon and Glass Fibers
- RheTech Products HP506-01 20% Talc Reinforced High Performance Polypropylene, Black
- Solvay Engineered Polymers SEQUEL® 2322 Engineered Polyolefin (discontinued **)
- Kazanorgsintez 102-15 Composition of Low Density Polyethylene, Crack-Proof
- Goodfellow Platinum 87/Rhodium 13Thermocouple Alloy
- Lubrizol Estane® AG 9550 Thermoplastic Polyurethane
- Eurostar Starflam P10002Z PA6, Flame Retardant, Extrusion
- DSM Akulon® K223-P2 Impact Modified Nylon 6 (European Grade) (Dry)
Copyright © lookpolymers.com All Rights Reserved