Samsung Cheil Industries Infino® SC-1220UR PC, Unreinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® SC-1220UR PC, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Temperature 23.0 °C |
0.20 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 22 g/10 min @Load 1.20 kg, Temperature 300 °C |
22 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 62.8 MPa | 9100 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 90 % | 90 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 90.2 MPa | 13100 psi | 10 mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa | 327 ksi | 10 mm/min; ASTM D790 |
| Izod Impact, Notched | 7.35 J/cm @Thickness 3.17 mm |
13.8 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C @Thickness 6.40 mm |
255 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 142 °C | 288 °F | B/50; ISO R306 |
| Flammability, UL94 | V-2 @Thickness 0.800 - 3.20 mm |
V-2 @Thickness 0.0315 - 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 0.20 % @Thickness 3.20 mm |
0.20 % @Thickness 0.126 in |
ASTM D1003 |
| Transmission, Visible | 90 % @Thickness 3.20 mm |
90 % @Thickness 0.126 in |
ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dissipation Factor | 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 110 sec | 110 sec | Tungsten; ASTM D495 |
Users viewing this material also viewed the following:
- Polykemi AB SCANAMID 66.6 C12^F30 Nylon 66/6, Glass Fiber, Reinforced
- Resin Technology Group Fusion 902 Odorless, Non-Frosting Fusion Cyanoacrylate
- Kraton® G1652 E (SEBS) Linear Triblock Copolymer
- KaMin Polygloss® 90 Kaolin Clay - Ultrafine, high brightness
- H.C. Starck Molybdenum Alloy AFB-3OW, Arc-Cast Forging Billet
- Chevron Phillips Marlex® 9346 HDPE Natural Pipe Resin
- DuPont Performance Polymers Delrin® 500AF Acetal (POM) (Unverified Data**)
- ExxonMobil 1000 Mobilgear SHC Series
- 3M 3513 Copper Foil Tape
Copyright © lookpolymers.com All Rights Reserved