SABIC Innovative Plastics LNP THERMOCOMP 9X11428J PPS
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 9X11428J PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* 9X11428J is a compound based on Polyphenylsulfone containing Proprietary Fillers. Added features of this material include: Healthcare, Low Extractable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.290 % | 0.290 % | 50% RH, 24 hrs; ASTM D570 |
| 0.400 % | 0.400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 |
| 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 15 % | 15 % | Type I, 5 mm/min; ASTM D638 |
| 22 % | 22 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 7.0 % | 7.0 % | 5 mm/min; ISO 527 |
| 8.0 % | 8.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.33 GPa | 338 ksi | 1 mm/min; ISO 527 |
| 2.38 GPa | 345 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 91.0 MPa | 13200 psi | ISO 178 |
| Flexural Modulus | 2.27 GPa | 329 ksi | 2 mm/min; ISO 178 |
| 2.43 GPa | 352 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.87 J/cm | 3.50 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 42.0 J @Temperature 23.0 °C |
31.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 44.0 J | 32.5 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 199 °C @Thickness 3.20 mm |
390 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products FT7012-707UV Thermoplastic Polyolefin, UV Stabilized, 848 Black
- Niche Polymer PPCG40BK Copolymer PP, 40% Glass Fiber Filled
- PolyOne Nymax™ GF 1200 A 13 Natural Polyamide 66 (Nylon 66)
- GrafTech GRAFOIL® GHW Standard Fluid Sealing Laminate, Non-Metal Reinforced
- LG Chemical Lupoy 1302HP-10 Polycarbonate Resin
- Solvay ALKAMULS® OL 40 Surfactant
- Eifeler Coatings Technology VARIANTA® TiAlN PVD Coating
- Ashley Polymers Ashlene® 64M Nylon 66
- Zoltek Pyron® Plain Weave Fabric Oxidized Pan Fiber
Copyright © lookpolymers.com All Rights Reserved