- Samsung Cheil Industries Infino® MKD-1016 PA, 55% Glass Filled
Samsung Cheil Industries Infino® MKD-1016 PA, 55% Glass Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® MKD-1016 PA, 55% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Water Absorption | 3.9 % @Temperature 23.0 °C |
3.9 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| 13 g/10 min @Load 2.16 kg, Temperature 275 °C |
13 g/10 min @Load 4.76 lb, Temperature 527 °F |
ASTM D1238 | |
| Ash | 55 % | 55 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength at Break | 265 MPa | 38400 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 265 MPa | 38400 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 4.2 % | 4.2 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 18.6 GPa | 2700 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 333 MPa | 48300 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 15.3 GPa | 2220 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.18 J/cm @Thickness 6.35 mm |
2.20 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.27 J/cm @Thickness 3.17 mm |
2.39 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C @Thickness 6.40 mm |
482 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 - 3.00 mm |
HB @Thickness 0.0315 - 0.118 in |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 7318 GREY
- Abatron 2217 A/B Filled Potting Compound (discontinued **)
- PolyOne Edgetek® AS-10GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
- Hannam Chemical Hanalac 775 ABS, Extrusion Grade
- SABIC Innovative Plastics NORYL PX6120 PPE+PS
- Teknor Apex Sinpolene MBW1072 Low Density Polyethylene
- Eastman Eastar MN021 Copolyester
- Chosun Refractories SSB-1 Bricks, Reaction Bonded SiC
- Abatron AboSeal 8104-8 Polysulfide, Thixotropic Sealant and Caulk
- Arlon 55359R062 62 mil Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved