SABIC Innovative Plastics LNP LUBRILOY ZX06315 PPE+SEBS+Polyolefin (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Styrene-Butadiene |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY ZX06315 PPE+SEBS+Polyolefin (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubriloy* ZX06315 is a compound based on PPE+PS Blend resin containing Flame Retardant, Proprietary Lubricant. Added features of this material include: Internally Lubricated, Non-Brominated & Non-Chlorinated Flame Retardant, Flame Retardant, high HDT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0094 - 0.0096 cm/cm @Time 86400 sec |
0.0094 - 0.0096 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0091 - 0.0093 cm/cm @Time 86400 sec |
0.0091 - 0.0093 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Index of Compound | 38 g/10 min @Load 10.0 kg, Temperature 280 °C |
38 g/10 min @Load 22.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 11.9 % | 11.9 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.27 GPa | 329 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.19 GPa | 318 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 2.30 J/cm | 4.31 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.21 | 0.21 | ASTM D3702 Modified |
| K (wear) Factor | 131 x 10-8 mm³/N-M | 65.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 720 µm/m-°C @Temperature -40.0 - 40.0 °C |
400 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 129 °C @Thickness 6.40 mm |
264 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 M2 Nylon 6.6 for injection molding, 2% molybdenum disulphide lubricated
- SABIC Innovative Plastics Lexan® HP1R PC
- Gwent Electronic Materials P2121112P7 Acid Vapor Plasma Modified Multiwalled Carbon Nanotubes
- Heraeus Cleviosâ„¢ PH 510 Conductive Sulfonate Polymer for Antistatic Coatings
- Techmer ES Luriblend® PE 5903
- A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene
- Zeon Chemicals Zetpol® 2010 Hydrogenated Nitrile Elastomomer
- Techmer ES HiFill® PA12 1100 Tungsten Filled
Copyright © lookpolymers.com All Rights Reserved