Ineos ABS Triax® KU 2-3050 ABS + Polyamide Blend (Conditioned)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Triax® KU 2-3050 ABS + Polyamide Blend (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightHeat stabilized or stable to heatSuitable processing methods:Injection molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | Melt |
| 1.06 g/cc | 0.0383 lb/in³ | (DAM) | |
| Water Absorption | 6.0 % | 6.0 % | (from DAM) |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 23°C/50% R.H. (from DAM) |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | |
| Melt Flow | 7.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | |
| Elongation at Break | >= 50 % | >= 50 % | Nominal |
| Elongation at Yield | 13 % | 13 % | |
| Tensile Modulus | 1.05 GPa | 152 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 7.40 J/cm² | 35.2 ft-lb/in² | |
| 1.60 J/cm² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
||
| Puncture Energy | 38.0 J | 28.0 ft-lb | Puncture energy +23°C |
| 40.0 J | 29.5 ft-lb | Puncture energy -30°C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 105 µm/m-°C @Temperature 20.0 °C |
58.3 µin/in-°F @Temperature 68.0 °F |
DAM |
| CTE, linear, Transverse to Flow | 115 µm/m-°C @Temperature 20.0 °C |
63.9 µin/in-°F @Temperature 68.0 °F |
DAM |
| Specific Heat Capacity | 2.20 J/g-°C | 0.526 BTU/lb-°F | Melt |
| Thermal Conductivity | 0.145 W/m-K | 1.01 BTU-in/hr-ft²-°F | Melt |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | (from DAM) |
| Vicat Softening Point | 102 °C | 216 °F | 50°C/h 50N (from DAM) |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
|
| 6.7 @Frequency 100 Hz |
6.7 @Frequency 100 Hz |
||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | |
| Dissipation Factor | 0.055 @Frequency 1e+6 Hz |
0.055 @Frequency 1e+6 Hz |
|
| 0.10 @Frequency 100 Hz |
0.10 @Frequency 100 Hz |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding |
| Ejection Temperature | 90.0 °C | 194 °F | |
| Injection Velocity | 40.0 mm/sec | 1.57 in/sec |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Effective thermal diffusivity | 0.732E-7 m²/s | Melt |
Users viewing this material also viewed the following:
- MV Labs PT465 K2PtCl6 Potassium hexachloroplatinate(IV)
- Mallard Creek Polymers ROVENE® 4487 SBR Latex
- Fujipoly Industries Gold 8000 Type B Connector
- LG Chemical LUMID GP3200A(W) PA6+MF20%, General Purpose
- MetalTek MTEK 21 UNS R30021 Cobalt Base Alloy
- Techmer ES HiFill® PA6 GF35 LE 35% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66
- Universal Wire Works Nichrome V (AMS 5676) Nickel Alloy Filler Metal
- Bulk Molding Compounds BMC SLC 1000 Glass Reinforced Polyester
- Industeel VIRGO 17.4PH 17Cr-4Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (480°C (900°F) - 1 hour + air cooled)
Copyright © lookpolymers.com All Rights Reserved