- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Samsung Cheil Industries Infino® HP-0500 ABS, Unreinforced Heat Resistant
Samsung Cheil Industries Infino® HP-0500 ABS, Unreinforced Heat Resistant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HP-0500 ABS, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS material that can mainly be used for the exterior material of household appliances etc.Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 220 °C |
20 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength at Break | 19.6 MPa | 2840 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 39 % | 39 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.55 GPa | 370 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 79.4 MPa | 11500 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.27 J/cm @Thickness 6.35 mm |
2.39 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.27 J/cm @Thickness 3.17 mm |
2.39 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C @Thickness 6.40 mm |
196 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 103 °C | 217 °F | B/50; ISO R306 |
| 105 °C | 221 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
Users viewing this material also viewed the following:
- PolyOne Versaflex™ OM 6258-9 Thermoplastic Elastomer (TPE)
- Outokumpu 4439 Austenitic Stainless Steel
- SABIC Innovative Plastics EXTEM XH1015 TPI Resin
- PolyChem Alloy PolyFast 8167UC
- Lehmann & Voss LUVOCOM® 1301-8349 PPS, linear, with PTFE
- Teknor Apex Telcar® TL-4145 Thermoplastic Elastomer
- Aclo Accucomp ABS ABS802L High Impact Grade
- Bapolene® 107A Low Density Polyethylene Film Extrusion Resin
- A. Schulman ComAlloy Comtuf® 410 Polycarbonate/Polyester Alloy
Copyright © lookpolymers.com All Rights Reserved