- HOME
- POLYMER SEARCH
- Thermoplastic
- Polycarbonate (PC)
- Polycarbonate, 10% Glass Filled
- Samsung Cheil Industries Infino® HN-3104 PC, 10% Glass Filled FR
Samsung Cheil Industries Infino® HN-3104 PC, 10% Glass Filled FR
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HN-3104 PC, 10% Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.20 mm |
0.0010 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm @Thickness 3.20 mm |
0.0010 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| 12.5 g/10 min @Load 10.0 kg, Temperature 250 °C |
12.5 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 | |
| Ash | 10.5 % | 10.5 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 53.9 MPa | 7820 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.9 MPa | 7820 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.43 GPa | 498 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 3.53 GPa | 512 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 6.35 mm |
1.47 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.981 J/cm @Thickness 3.17 mm |
1.84 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C @Thickness 6.40 mm |
282 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C @Thickness 6.40 mm |
284 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 - 3.00 mm |
V-0 @Thickness 0.0591 - 0.118 in |
|
| Glow Wire Test | 960 °C @Thickness 1.50 mm |
1760 °F @Thickness 0.0591 in |
IEC 60695-2-12 |
Users viewing this material also viewed the following:
- RheTech Products G40P100-04UV 40% Glass Fiber Reinforced Polypropylene, UV Stabilized, White
- SABIC 120W Linear Low Density Polyethylene for Blown Film
- Global PEI-110 Easy Flow, Polyetherimide
- SABIC Innovative Plastics ULTEM HU1000E PEI (Asia Pacific)
- Teknor Apex APEX® 3701-60NT Polyvinyl Chloride, Flexible
- A. Schulman PAPERMATCH® H-5338 Specialty Masterbatch
- Cotronics Resbond™ 940 High Temperature Ceramic Adhesive, Fast Set
- EMS-Griltech Grilon® TN 2200 White Nylon 6 Fiber
- Alliance Polymers Viprene™ P60A-22U-NAT Thermoplastic Vulcanizate Elastomer
- ExxonMobil Exceed™ 3527PA Metallocene Polyethylene Resin (European Grade)
Copyright © lookpolymers.com All Rights Reserved