Samsung Cheil Industries Infino® HA-1011 PC/ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® HA-1011 PC/ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 0.15 % @Temperature 23.0 °C |
0.15 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 49 g/10 min @Load 10.0 kg, Temperature 250 °C |
49 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength at Break | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 46.1 MPa | 6680 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 115 % | 115 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.77 GPa | 256 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 68.6 MPa | 9950 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 3.92 J/cm @Thickness 6.35 mm |
7.35 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 7.06 J/cm @Thickness 3.17 mm |
13.2 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C @Thickness 6.40 mm |
223 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 117 °C | 243 °F | B/50; ISO R306 |
| 120 °C | 248 °F | B/120; ISO R306 |
Users viewing this material also viewed the following:
- Oxford Polymers 25GB-5GF-IM Polybutylene Terephthalate (PBT), Impact Modified/ Glass Beads
- DuPont™ Clysar® EZ Polyolefin Shrink Packaging Film, 60 Gauge (discontinued **)
- Kennametal Stellite Stellite® 706 Cobalt Alloy
- SGL Carbon Group PANOX® SM C063 EEA Oxidized Textile Fiber, Crimped staple fiber, For carbon/carbon and spinning
- SABIC Innovative Plastics NORYL GTX GTX230 PPE+PA66 (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- Goodfellow Nickel 70/Zirconium 30 Alloy
- Lubrizol ESTANE® 5701 Ester Based Thermoplastic Polyurethane
- Arkema Group Rilsan® AMN D Nylon 12, Rigid, Injection Grade (Dry)
- 3M Safety-Walk™ 630 Safety Yellow Slip-Resistant General Purpose Tapes and Treads
Copyright © lookpolymers.com All Rights Reserved