- Samsung Cheil Industries Infino® GP-5000 PBT, Unreinforced
Samsung Cheil Industries Infino® GP-5000 PBT, Unreinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® GP-5000 PBT, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General PBT material that can be used for connectorsInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.021 cm/cm @Thickness 3.20 mm |
0.012 - 0.021 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 74 g/10 min @Load 2.16 kg, Temperature 250 °C |
74 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength at Break | 46.1 MPa | 6690 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.9 MPa | 7820 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.16 GPa | 313 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.26 GPa | 327 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.265 J/cm @Thickness 6.35 mm |
0.496 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.275 J/cm @Thickness 3.17 mm |
0.514 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C @Thickness 6.40 mm |
338 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C @Thickness 6.40 mm |
167 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 188 °C | 370 °F | B/50; ISO R306 |
| 188 °C | 370 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 0.700 mm |
HB @Thickness 0.0276 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 140 sec | 140 sec | Tungsten; ASTM D495 |
Users viewing this material also viewed the following:
- BP Amoco Acctuf® 3045 Impact Copolymer Polypropylene (discontinued **)
- Lehmann & Voss LUVOCOM® 19-7278 Polyamide 46, with carbon fiber
- SABIC Innovative Plastics LNP LUBRICOMP RAL22I PA 66
- Wanhua Chemical Wanthane® WHT-1198 Polyester Based TPU
- Tra-Con Tra-Bond 216D01 Dam/Fill Applications Adhesive
- Trelleborg R510 Commercial Natural Rubber Polyisoprene
- UBE Tyranno Grade G Ceramic Semi-Conductive Fiber
- PolyOne Edgetek® MP-1000 Modified PPO - Unreinforced (discontinued **)
- PolyOne Elastamax XL-0257-2 TPU-Based Thermoplastic Elastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved