TSE Industries Millathane® CM High Temperature-Resistant Millable Polyester Polyurethane

Category	Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer	TSE Industries, Inc
Trade Name	Millathane®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	TSE Industries Millathane® CM High Temperature-Resistant Millable Polyester Polyurethane.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear strength, oil and fuel resistance, and ozone resistance. The life expectancy of urethane is often 5 times longer than other elastomers, thus saving material costs and downtime expense. One shortcoming of polyurethanes is loss of physical properties at temperatures over 180°F (82°C). MILLATHANE HT has overcome this weakness.All information provided by TSE Industries

Physical Properties	Metric	English	Comments
Specific Gravity	1.12 g/cc	1.12 g/cc
Mooney Viscosity	35 - 65 @Temperature 100 °C	35 - 65 @Temperature 212 °F	ML 1+4
	40 - 60 @Temperature 100 °C	40 - 60 @Temperature 212 °F	Standard, ML 1+4

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	30 - 90	30 - 90
Tensile Strength, Yield	<= 27.6 MPa	<= 4000 psi
Resilience	20 - 40	20 - 40	%

Thermal Properties	Metric	English	Comments
Brittleness Temperature	-59.0 °C	-74.2 °F

Descriptive Properties	Value	Comments
Abrasion Resistance	Excellent
Appearance	Dark to light amber solid bale or milled sheets
Elongation	Good
Health Hazard	None
Heat Aging Resistance	Excellent to 250ºF continuous, 300ºF intermittent
Odor	Faint, characteristic
Oil and Fuel Resistance	Excellent
Ozone Resistance	Excellent
Storage Stability	Excellent
Tear Resistance	Excellent
Weather Resistance	Excellent