SYNTHOS Forsan® 573 L Acrylonitrile Butadiene Styrene (ABS)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SYNTHOS Kralupy a.s. |
| Trade Name | Forsan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SYNTHOS Forsan® 573 L Acrylonitrile Butadiene Styrene (ABS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Increased heat resistant, glossy, UV stabilized.Applications: Electrotechnics, automotiveHousehold appliances, office equipment, car interior parts, profiles, ABS sheets, etc.Synthos was formerly known as Kaucuk. All information provided by Synthos.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | Internal; 50x50mm |
| Melt Flow | 10.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
10.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
Granulate; ISO 1133/U |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
80x10x4mm, r=0.25; V-notch; ISO 180/1A |
| Charpy Impact Unnotched | 16.0 J/cm² @Temperature 23.0 °C |
76.1 ft-lb/in² @Temperature 73.4 °F |
80x10x4mm; ISO 179/1eU |
| Charpy Impact, Notched | 1.70 J/cm² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
80x10x4mm, r=0.25; V-notch; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 100 °C | 212 °F | 50°C/h; 50N; 10x10x4mm; ISO 306/B50 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Tested in EZÚ Praha |
| Glow Wire Test | 650 °C | 1200 °F | Ø 93x3mm; IEC 60695-2-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | 500V; Ø 93x3mm; IEC 60093 |
| Surface Resistance | 5.00e+15 ohm | 5.00e+15 ohm | 500V; Ø 93x3mm; IEC 60093 |
| Dielectric Constant | 2.6 @Frequency 1e+6 Hz |
2.6 @Frequency 1e+6 Hz |
Ø 50x3mm; IEC 60250 |
| <= 2.7 @Frequency 50 Hz |
<= 2.7 @Frequency 50 Hz |
Ø 50x3mm; IEC 60250 | |
| Dielectric Strength | 12.0 kV/mm @Thickness 3.00 mm |
305 kV/in @Thickness 0.118 in |
Transformer Oil; IEC 60243-1 |
| 53.0 kV/mm @Thickness 0.500 mm |
1350 kV/in @Thickness 0.0197 in |
Transformer Oil; IEC 60243-1 | |
| Dissipation Factor | 0.0050 @Frequency 50 Hz |
0.0050 @Frequency 50 Hz |
Ø 93x3mm; IEC 60250 |
| 0.0080 @Frequency 1e+6 Hz |
0.0080 @Frequency 1e+6 Hz |
Ø 93x3mm; IEC 60250 | |
| Arc Resistance | 92 sec | 92 sec | Ø 93x3mm; IEC 61621 |
| Comparative Tracking Index | 400 V | 400 V | Solution A; Ø 93x3mm; IEC 60112 |
Users viewing this material also viewed the following:
- Ineos Nova 2511 General Purpose Crystal Polystyrene (discontinued **)
- Samyang Trirex® 3030IR Polycarbonate
- SABIC Innovative Plastics LNP THERMOCOMP ZF006 PPE+PS (Asia Pacific)
- A. Schulman POLYBATCH™ Hot Pink 50377 Concentrate Based In Polyethylene
- Covestro Bayblend® KU 2-1480 Polycarbonate/ABS Blend
- Dow SE BR-1202D Stereospecific high cis-1,4 Polybutadiene (BR)
- Eurotec® Tecopet® PT70 GR15 NL100 PS20 PET, 15% glass fiber reinforced, flame retardant - halogen (RoHS compliant), heat stabilized, natural, fast crystallization grade
- Henkel Hysol EA 9394/C-2 Paste Adhesive System
Copyright © lookpolymers.com All Rights Reserved