SSAB Tunnplat Domex® 315MC HSLA Steel
| Category | Metal , Ferrous Metal , Alloy Steel , Low Alloy Steel |
| Manufacturer | SSAB Tunnplat AB |
| Trade Name | Domex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SSAB Tunnplat Domex® 315MC HSLA Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
HSLA SteelCharacteristics: For hot-dip galvanizing, a thin Zn coating (50-80 microns) is specified.Domex® MC grade steels conform to the provisions of EN 10149-2 standard and often have better properties.Property data is for hot-rolled steel.Domex® is the brand name of hot rolled products from SSAB Tunnplat. Domex® cold-forming steels are modern structural steels. General use of Domex® high strength steels offers a number of benefits compared to ordinary structural steels: Lower weight, Simpler production, Lower creep rate, Longer useful life, Higher load-bearing capacity, Lower transport costs, Reduced stocks, Lower overall cost.Data provided by SSAB Tunnplat.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.87 g/cc | 0.284 lb/in³ | Estimated by MatWeb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 390 - 510 MPa | 56600 - 74000 psi | |
| Tensile Strength, Yield | >= 315 MPa | >= 45700 psi | |
| Elongation at Break | >= 20 % @Thickness >=3.00 mm |
>= 20 % @Thickness >=0.118 in |
A<sub>80</sub> |
| >= 24 % @Thickness >=3.00 mm |
>= 24 % @Thickness >=0.118 in |
A<sub>5</sub> | |
| Bend Radius, Minimum | >= 0.25 t | >= 0.25 t | t<3mm; internal bend radius, 90° |
| >= 0.50 t | >= 0.50 t | 3 mm < t< 6mm; internal bend radius, 90° | |
| >= 0.80 t | >= 0.80 t | t>6mm; internal bend radius, 90° |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | >= 0.015 % | >= 0.015 % | |
| Carbon, C | <= 0.10 % | <= 0.10 % | |
| Iron, Fe | 98 % | 98 % | As remainder |
| Manganese, Mn | <= 1.3 % | <= 1.3 % | |
| Niobium, Nb (Columbium, Cb) | <= 0.090 % | <= 0.090 % | |
| Phosphorous, P | <= 0.025 % | <= 0.025 % | |
| Silicon, Si | <= 0.030 % | <= 0.030 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Titanium, Ti | <= 0.15 % | <= 0.15 % | |
| Vanadium, V | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- MV Labs Y300 Y2(CO3)3·xH2O Yttrium carbonate hydrate
- MarkeTech Magnesium Oxide (MgO) Single Crystal Substrate
- Solvay Specialty Polymers FOMBLIN® Y04 PFPE Lubricant
- Special Metals NIMONIC® Alloy 80A
- SK Chemicals SKYTHANE® 190A S series Polyurethane
- Borealis Superclean™ LR4201S Crosslinkable Polyethylene Insulation for Medium and High Voltage Power Cables
- Chase Plastics CP Pryme® N110GL (COND, 50% RH) Nylon 6, 10% Glass Fiber Reinforced, Internally Lubricated
- Covestro Bayfol® AS-A 2-4 Polycarbonate + PBT
- Entec Hypro™ PP-HP12NS Homopolymer, 12 Melt Flow, Nucleated, Anti-stat, Injection Molding
Copyright © lookpolymers.com All Rights Reserved