Polyram PlusTek RA300G3 Nylon 6.6, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA300G3 Nylon 6.6, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | DIN 53479 |
| Water Absorption | 0.90 % | 0.90 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 100 MPa | >= 14500 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | >= 155 MPa | >= 22500 psi | ASTM D790 |
| Flexural Modulus | >= 4.00 GPa | >= 580 ksi | ASTM-D790 |
| Izod Impact, Notched | >= 0.300 J/cm @Temperature 23.0 °C |
>= 0.562 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 200 °C | >= 392 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 180 °C | >= 356 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Sichuan Deyang Haton® 440 dtex Polyphenylene Sulfide Filament
- Silberline Silvex® 225-20-D
- ScanTube MFA Tubing
- Trelleborg Emerson & Cuming Eccobond® 51 Two-Component General Purpose Epoxy Adhesive
- Cheng Yu Plastic ML3435 PC, 35% Glass Fiber
- Dow LDPE 4012M Low Density Polyethylene
- Beijing Ranger Chem WSR615 Liquid Epoxy Resin
- Asahi Kasei Thermofil P-20TC-5100R 20% Talc Filled, Heat Stabilized
- Asia International Enterprise (Hong Kong) 30G3 Polybutylene terephthalate, 15% Glass Fiber Filled
Copyright © lookpolymers.com All Rights Reserved