Borealis LE0151 Easy Strippable Semiconductive Insulation Shield for Medium Voltage Power Cables

Category Polymer , Thermoplastic , Polyolefin , Polyolefin, Wire/Cable Grade
Manufacturer Borealis
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis LE0151 Easy Strippable Semiconductive Insulation Shield for Medium Voltage Power Cables.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LE0515 is an easy strippable crosslinkable semi conductive insulation shield compound designed for medium voltage (5kV-46kV) power cable applications. Application: LE0515 is especially suitable for use in triple extrusion processes. Strip forces in the range of 0.85 – 2.15 kN/m (2-5 lbs/0.5” have been found on cables from dry cure vulcanization lines. Stripping of LE0515 from the surface of the insulation is readily initiated, and it continues easily over a wide range of temperatures without tearing. It leaves a clean insulation surface. Specifications: IEC 60502; BS 6622; NF C33-223/UTE C33-223/NF C33-226; AEIC CS 8-00; ICEA S-94-649; and ICEA S-97-682.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ASTM D1928C/D 792
Mechanical Properties Metric English Comments
Tensile Strength at Break 9.90 MPa
1440 psi
after aging 7 days @ 136°C
11.0 MPa
1600 psi
ASTM D412
Elongation at Break >= 100 %
>= 100 %
after aging 7 days @ 136°C
250 %
250 %
ASTM D412
Electrical Properties Metric English Comments
Volume Resistivity 100 ohm-cm

@Temperature 23.0 °C
100 ohm-cm

@Temperature 73.4 °F
ASTM D991
100 ohm-cm

@Temperature 90.0 °C
100 ohm-cm

@Temperature 194 °F
ASTM D991
Processing Properties Metric English Comments
Zone 1 49.0 °C
120 °F
Zone 2 82.0 °C
180 °F
Zone 3 93.0 °C
199 °F
Zone 4 104 °C
219 °F
Die Temperature 115 °C
239 °F
Die Cooling Temperature 25.0 °C
77.0 °F
hopper cooling