SABIC Innovative Plastics Valox® V8090 PBT+PET (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + PET Blend, Glass Filled , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® V8090 PBT+PET (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
50% Glass Fiber Reinforced PBT-PET resin
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.16 % | 0.16 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0050 cm/cm | 0.0010 - 0.0050 in/in | on Tensile Bar; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 7.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 175 MPa | 25400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 17.5 GPa | 2540 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 255 MPa | 37000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| 40.0 kJ/m² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
8.33 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
40.0 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 210 °C | 410 °F | Rate B/120; ISO 306 |
| 212 °C | 414 °F | Rate B/50; ISO 306 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V75Y Fluoroelastomer Compound
- Lehmann & Voss LUVOCOM® 1502-7867/BL4 PPSU, unreinforced
- LATI Kelon® B H CER/30 PA 6, 30% Mineral Reinforced, Heat Stabilized
- Sylvin Technologies 9077-80 Natural PVC for Injection Molding
- SABIC Innovative Plastics ULTEM DT1810EV PEI Blend
- Teknor Apex Telcar® TL-1081B Thermoplastic Elastomer
- Esstech X-127-0950 Poly Methyl Methacrylate
- Eurostar Staramide PK005EI2 PA6, Mineral Fiber Filled, Impact Modified Injection Molded
- Colorite Polymers 8804 General Purpose Vinyl Compound
- Asahi Kasei Leona® 1700S Nylon 66
Copyright © lookpolymers.com All Rights Reserved