SABIC Innovative Plastics Valox® IQ420HP PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® IQ420HP PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Environmentally responsible, low carbon footprint Valox iQ* resin - Valox* iQ420HP resin is made using iQ-PBT resin and 30% glass fiber reinforcement. Valox* iQ420HP may be used for the production of food contact articles intended for repeat use (and not for single use) in contact with all food types, and under all conditions of use per FDA table of food types, with the exception of irradiation and cooking/baking at temperatures above 250 degrees F. This includes microwaving within these same temperature constraints. If colorants are added to the resin, these must be evaluated separately for their appropriateness for food contact applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.090 % | 0.090 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 52 g/10 min @Load 5.00 kg, Temperature 250 °C |
52 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 38 g/10 min @Load 5.00 kg, Temperature 250 °C |
38 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
| 139 MPa | 20200 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
| 139 MPa | 20200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.6 % | 1.6 % | 5 mm/min; ISO 527 |
| 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 10.7 GPa | 1550 ksi | 1 mm/min; ISO 527 |
| 11.8 GPa | 1710 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 210 MPa | 30500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 210 MPa | 30500 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 9.10 GPa | 1320 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.10 GPa | 1320 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.820 J/cm | 1.54 ft-lb/in | ASTM D256 |
| 0.830 J/cm @Temperature -30.0 °C |
1.55 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 7.70 J/cm | 14.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 25.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 89.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 89.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
49.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Hot Ball Pressure Test | <= 200 °C | <= 392 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 203 °C @Thickness 3.20 mm |
397 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 206 °C | 403 °F | Rate B/50; ASTM D1525 |
| 206 °C | 403 °F | Rate B/50; ISO 306 | |
| 206 °C | 403 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with Benzoflex 9-88SG
- Kolon KOPA® KN333G35CR G/F Reinforced Nylon 66
- H.C. Starck Grade UF 05 Silicon Carbide, SiC
- Techmer ES HiFill® PA6 GF15 HS L 15% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP RF006L PA 66
- Formosa Plastics Formolene® L62009A Film (Hexene Grade) LLDPE
- DuPont Teijin Films Teijin® Tetoron® HB3 Polyester Film, 200 Gauge
- Ferro EG 2800 Metal Sealing
- Gwent Electronic Materials R2070613P2 Resin Binder
Copyright © lookpolymers.com All Rights Reserved