- Eurostar Starglas OC004 PPS, 20% Carbon Filled, Injection Molded
Eurostar Starglas OC004 PPS, 20% Carbon Filled, Injection Molded
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starglas |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starglas OC004 PPS, 20% Carbon Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starglas OC004 is a 20% Carbon Fiber Reinforced PPS Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Water Absorption | 0.040 % @Temperature 23.0 °C, Time 86400 sec |
0.040 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm @Thickness 4.00 mm |
0.0015 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 144 MPa | 20900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.1 % | 1.1 % | 5 mm/min; ISO 527 |
| 1.5 % | 1.5 % | Flexural, 2 mm/min; ISO 178 | |
| Tensile Modulus | 16.6 GPa | 2410 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 193 MPa | 28000 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 194 MPa | 28100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 15.1 GPa | 2190 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 13.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
7.22 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
30.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 275 °C | 527 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 205 - 315 °C | 401 - 599 °F | |
| Zone 2 | 320 - 330 °C | 608 - 626 °F | |
| Zone 3 | 330 - 345 °C | 626 - 653 °F | |
| Melt Temperature | 315 - 320 °C | 599 - 608 °F | |
| Mold Temperature | 140 - 165 °C | 284 - 329 °F | |
| Drying Temperature | 120 - 150 °C @Time 14400 sec |
248 - 302 °F @Time 4.00 hour |
Users viewing this material also viewed the following:
- PTS Tristar® PC-10R-CL(V15) 15 MFI UV Stabilized Clear Polycarbonate with Release
- SABIC Innovative Plastics Lexan® FST3403 PC Copolymer
- H.C. Starck Pure Molybdenum, Sheet Premium Grade PS-100-2
- Techmer ES Electrafil® J-1/CF/10 Nylon 66, 10% Carbon Fiber Reinforced
- Solvay Specialty Polymers Polymist® XPP 538 Polytetrafluoroethylene (PTFE)
- SABIC Innovative Plastics LNP Stat-kon ZE004 MODIFIED POYPHENYLENE
- Chisso Z CLEAN® E3001 Purging Solution
- DSM Arnite® TV6 260 T PBT-I-GF30
- LG Chemical SG175G ABS, Super Surface Gloss, High Flow
- Amco Amalloy® B9575 Polymer Alloy
Copyright © lookpolymers.com All Rights Reserved