SABIC Innovative Plastics Ultem ATX153R PEI+PCE

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem ATX153R PEI+PCE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.47 g/cc
1.47 g/cc
ASTM D 792
Density 1.47 g/cc
0.0531 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %

@Temperature 23.0 °C
 0.50 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
on tensile bar; SABIC Method
0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0040 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0050 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 28 g/10 min

@Load 5.00 kg,
Temperature 360 °C
 28 g/10 min

@Load 11.0 lb,
Temperature 680 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
30 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 30 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 143 MPa
20700 psi
5 mm/min; ISO 527
144 MPa
20900 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 143 MPa
20700 psi
5 mm/min; ISO 527
144 MPa
20900 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 2.4 %
2.4 %
5 mm/min; ISO 527
2.5 %
2.5 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 2.4 %
2.4 %
5 mm/min; ISO 527
2.5 %
2.5 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 9.68 GPa
1400 ksi
1 mm/min; ISO 527
9.69 GPa
1410 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 203 MPa
29400 psi
1.3 mm/min, 50 mm span; ASTM D 790
218 MPa
31600 psi
2 mm/min; ISO 178
Flexural Modulus 8.61 GPa
1250 ksi
1.3 mm/min, 50 mm span; ASTM D 790
8.72 GPa
1260 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.07 J/cm

@Temperature 23.0 °C
 2.00 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 8.54 J/cm

@Temperature 23.0 °C
 16.0 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 47.0 kJ/m²

@Temperature 23.0 °C
 22.4 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
49.0 kJ/m²

@Temperature -30.0 °C
 23.3 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched 5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
5.50 J/cm²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²

@Temperature 23.0 °C
 3.81 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.800 J/cm²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 15.0 J

@Temperature 23.0 °C
 11.1 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 18.0 µm/m-°C

@Temperature -40.0 - 150 °C
 10.0 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
18.0 µm/m-°C

@Temperature 23.0 - 150 °C
 10.0 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 58.0 µm/m-°C

@Temperature -40.0 - 150 °C
 32.2 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
58.0 µm/m-°C

@Temperature 23.0 - 150 °C
 32.2 µin/in-°F

@Temperature 73.4 - 302 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 180 °C
356 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
191 °C

@Thickness 3.20 mm
 376 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
193 °C

@Thickness 6.40 mm
 379 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 169 °C
336 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
182 °C

@Thickness 3.20 mm
 360 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
185 °C

@Thickness 6.40 mm
 365 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Vicat Softening Point 190 °C
374 °F
Rate B/50; ISO 306
192 °C
378 °F
Rate B/120; ISO 306
193 °C
379 °F
Rate B/50; ASTM D 1525
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
5VA

@Thickness 3.00 mm
 5VA

@Thickness 0.118 in
 UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1.10e+16 ohm-cm
1.10e+16 ohm-cm
IEC 60093
Surface Resistance 2.30e+16 ohm
2.30e+16 ohm
ROA; IEC 60093
Dielectric Strength 23.0 kV/mm

@Thickness 1.60 mm
 584 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
Dissipation Factor 0.0035

@Frequency 1000 Hz
 0.0035

@Frequency 1000 Hz
 IEC 60250
0.0037

@Frequency 50.0 - 60.0 Hz
 0.0037

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0096

@Frequency 1.00e+6 Hz
 0.0096

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 125 V
125 V
IEC 60112
>= 125 V
>= 125 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2