SABIC Innovative Plastics Ultem 1000M PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem 1000M PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D 792
Water Absorption 0.25 %

@Time 86400 sec
 0.25 %

@Time 24.0 hour
 ASTM D 570
Moisture Absorption at Equilibrium 1.25 %

@Temperature 23.0 °C
 1.25 %

@Temperature 73.4 °F
 ASTM D 570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 9.7 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 9.7 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 109
109
ASTM D 785
Tensile Strength, Yield 110 MPa
16000 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 60 %
60 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 7.0 %
7.0 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 3.58 GPa
519 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 165 MPa
23900 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 3.51 GPa
509 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Poissons Ratio 0.30
0.30
ASTM D 638
Shear Modulus 1.38 GPa
200 ksi
Calculated
Izod Impact, Notched 0.530 J/cm

@Temperature 23.0 °C
 0.993 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
16.02 J/cm

@Thickness 3.20 mm
 30.01 ft-lb/in

@Thickness 0.126 in
 reverse notched; ASTM D 256
Izod Impact, Unnotched 13.35 J/cm

@Temperature 23.0 °C
 25.01 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Gardner Impact 36.0 J

@Temperature 23.0 °C
 26.6 ft-lb

@Temperature 73.4 °F
 ASTM D 3029
Taber Abrasion, mg/1000 Cycles 10

@Load 1.00 kg
 10

@Load 2.20 lb
 CS-17; ASTM D 1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.8 µm/m-°C

@Temperature -20.0 - 150 °C
 31.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
CTE, linear, Transverse to Flow 54.0 µm/m-°C

@Temperature -20.0 - 150 °C
 30.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
Thermal Conductivity 0.220 W/m-K
1.53 BTU-in/hr-ft²-°F
ASTM C 177
Deflection Temperature at 0.46 MPa (66 psi) 210 °C

@Thickness 6.40 mm
 410 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 201 °C

@Thickness 6.40 mm
 394 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Vicat Softening Point 218 °C
424 °F
Rate B/50; ASTM D 1525
Glass Transition Temp, Tg 217 °C
423 °F
Flammability, UL94 V-0

@Thickness 0.400 mm
 V-0

@Thickness 0.0157 in
 UL 94
NBS Smoke Density 0.70

@Time 240 sec
 0.70

@Time 0.0667 hour
 Flaming, Ds; ASTM E 662
Oxygen Index 47 %
47 %
LOI; ASTM D 2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D 257
Dielectric Constant 3.15

@Frequency 1000 Hz
 3.15

@Frequency 1000 Hz
 ASTM D 150
Dielectric Strength 27.9 kV/mm

@Thickness 1.60 mm
 709 kV/in

@Thickness 0.0630 in
 in oil; ASTM D 149
32.7 kV/mm

@Thickness 1.60 mm
 831 kV/in

@Thickness 0.0630 in
 in air; ASTM D 149
Dissipation Factor 0.0013

@Frequency 1000 Hz
 0.0013

@Frequency 1000 Hz
 ASTM D 150
0.0025

@Frequency 2.45e+9 Hz
 0.0025

@Frequency 2.45e+9 Hz
 ASTM D 150