Latrobe Lescalloy® 4335+V VAC-ARC High Strength Alloy Steel
| Category | Metal , Ferrous Metal , Alloy Steel , Low Alloy Steel , Carbon Steel , High Carbon Steel |
| Manufacturer | Latrobe Steel |
| Trade Name | Lescalloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Latrobe Lescalloy® 4335+V VAC-ARC High Strength Alloy Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
4335+V VAC-ARC is a low alloy steel with good strength and high hardenability. In addition, uniform properties are obtained in large sections. The alloy can be heat treated to strength values within a wide range and becomes superior to other low alloy steels above the 200,000 psi strength level. Lescalloy 4335+V VAC-ARC steel is produced by the vacuum consumable electrode melting process to provide optimum cleanliness and preferred ingot structure.Information Provided by Timken Latrobe Steel.Timken sold Latrobe in December 2006. They are now Latrobe Specialty Steels Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.83 g/cc | 0.283 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 56 | 56 | 1" from quench end; Jominy End Quench Hardenability |
| 56.5 | 56.5 | 1/2" from quenched end; Jominy End Quench Hardenability | |
| 58 | 58 | 1/8" from quenched end; Jominy End Quench Hardenability | |
| Tensile Strength, Ultimate | 931 MPa | 135000 psi | 1200°F Temper |
| 1520 MPa | 220000 psi | 700°F Temper Temperature | |
| 1760 MPa | 255000 psi | 460°F Temper Temperature | |
| Tensile Strength, Yield | 1378 MPa @Strain 0.200 % |
199900 psi @Strain 0.200 % |
700°F Temper Temperature |
| 1448 MPa @Strain 0.200 % |
210000 psi @Strain 0.200 % |
460°F Temper Temperature | |
| Elongation at Break | 8.0 % | 8.0 % | 460°F Temper |
| 9.0 % | 9.0 % | 700°F Temper Temperature | |
| 16 % | 16 % | 1200°F Temper | |
| Reduction of Area | 30 % | 30 % | 460°F Temper Temperature |
| 35 % | 35 % | 700°F Temper Temperature |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.34 µm/m-°C @Temperature -17.8 - 648 °C |
6.300 µin/in-°F @Temperature -0.0400 - 1200 °F |
|
| Thermal Conductivity | 37.46 W/m-K | 260.0 BTU-in/hr-ft²-°F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.35 % | 0.35 % | |
| Chromium, Cr | 0.80 % | 0.80 % | |
| Iron, Fe | 95.2 % | 95.2 % | |
| Manganese, Mn | 0.75 % | 0.75 % | |
| Molybdenum, Mo | 0.35 % | 0.35 % | |
| Nickel, Ni | 1.85 % | 1.85 % | |
| Silicon, Si | 0.50 % | 0.50 % | |
| Vanadium, V | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Eastman Eastar 5445 PCTG Copolyester, Injection Molded (discontinued **)
- Kingfa HR-527B Modified ABS
- Fujipoly Industries Sarcon® GR-HFk Gap Filler Pad
- Karina E 500D08/201 Beige PVC Compound
- SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP STAT-KON OE008A PPS - Branched (Europe-Africa-Middle East)
- Teknor Apex APEX® 89-P129A-NT Polyvinyl Chloride, Flexible
- A. Schulman POLYFLAM™ CFP 4611 11% CACO3 filled copolymer polypropylene product
- Tra-Con Tra-Duct 916H01 Electronically Conductive Silver-Filled Epoxy
- DuPont™ Nomex® 410 Paper, 12 mil Nominal Thickness
Copyright © lookpolymers.com All Rights Reserved