SABIC Innovative Plastics ULTEM SF2260 PEI Blend (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM SF2260 PEI Blend (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Ultem for thin wall application
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 0.14 % @Time 86400 sec |
0.14 % @Time 24.0 hour |
ISO 62-1 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH |
| Linear Mold Shrinkage, Flow | 0.0046 cm/cm | 0.0046 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0054 cm/cm | 0.0054 in/in | SABIC Method |
| Melt Flow | 30 g/10 min @Load 6.60 kg, Temperature 337 °C |
30 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 70 g/10 min @Load 10.0 kg, Temperature 345 °C |
70 g/10 min @Load 22.0 lb, Temperature 653 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 142 MPa | 20600 psi | 5 mm/min; ISO 527 |
| 148 MPa | 21500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 9.40 GPa | 1360 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 191 MPa | 27700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.17 GPa | 1040 ksi | 2 mm/min; ISO 178 |
| 7.36 GPa | 1070 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature -40.0 - 150 °C |
7.78 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 18.0 µm/m-°C @Temperature 23.0 - 150 °C |
10.0 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.0 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 67.0 µm/m-°C @Temperature 23.0 - 150 °C |
37.2 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPO D 5308-20 BLK
- PolyOne Geon™ Vinyl Wire & Cable W1104L-xx40D Polyvinyl Chloride, Flexible (PVC, Flexible)
- I. Stern 550 High Impact Polystyrene
- KKPC KOSYN KNB 25H Acrylonitrile Butadiene Rubber (NBR)
- Momentive Performance Materials Siloprenâ„¢ LSR 7060 High Clarity Liquid Silicone Rubber
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 200 lb
- Shandong Dongyue Shenzhou New Material Co CHF090 Perfluorosulfonic Acid Ion-Exchange Resin (PFSA)
- Polyram RamTough RZ300G2 Polycarbonate, 10% Glass Fiber
- Braskem LHB118/21AF Blown Film Extrusion Linear Low Density Polyethylene
- Loctite® 564 Thread Sealant
Copyright © lookpolymers.com All Rights Reserved