NOVA Chemicals Novapol® PF-Y821-B Butene LLDPE Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Butene, Film |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NOVA Chemicals Novapol® PF-Y821-B Butene LLDPE Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Film Properties. Features: Good stiffness and machinability, good clarity with LDPE.Applications: General purpose packaging, liners.Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D792 |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 690 % | 690 % | ASTM D882 |
| Secant Modulus, MD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.230 GPa | 33.4 ksi | ASTM D882 |
| Coefficient of Friction | <= 0.25 | <= 0.25 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 3.30 g/micron | 83.8 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 13.8 g/micron | 351 g/mil | ASTM D1922 |
| Dart Drop | 3.50 g/micron | 88.9 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 38.0 MPa | 5510 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 27.0 MPa | 3920 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 12 % @Thickness 0.0250 mm |
12 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 50 % | 50 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 195 - 220 °C | 383 - 428 °F |
Users viewing this material also viewed the following:
- Covestro Apec® DP9-9354T High-Heat Polycarbonate, Transparent, Flame-Retardant (discontinued **)
- Taiwan Sheen Soon Sheenthane® A7810H TPU for Ink
- Shandong Dongyue Polymer DF-21B PTFE Presintered Resin
- SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Europe-Africa-Middle East)
- Formosa Plastics Formolon® 165 PVC
- Ecomass® 1002ZD96 Tungsten Filled COPA
- CP-Polymer-Technik Wellamid® 6000 GVS 20/10 HWCP 20% Glass Fiber and 10% Glass Sphere Nylon 6, Heat Stabilized, Dry
- Clariant Renol PA111G35IF Nylon 66, 35% Glass Fiber, Improved Flow
- ConocoPhillips HD Fleet™ 50 Engine Oil
Copyright © lookpolymers.com All Rights Reserved